AA Standards Grade 5454 O – Comprehensive Aluminium Alloy Specification
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.69 g/cm³ | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 70.0 GPa | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 | |
Hardness, Brinell | 62.0 [-] | O | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Tensile strength | 215.0 - 285.0 MPa | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 | |
250.0 MPa | O | AA Standards |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.36e-05 1/K | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 | |
100 °C | 2.36e-05 1/K | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 | ||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 600.0 - 645.0 °C | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 134 W/(m·K) | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 20000000.0 S/m | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Electrical resistivity | 5e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.05 - 0.2 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Copper | 0.1 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Iron | 0.40 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Magnesium | 2.4 - 3.0 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Manganese | 0.5 - 1.0 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Silicon | 0.25 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Titanium | 0.2 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Zinc | 0.25 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32, H111), sufficient (H34) | |
| Workability | general (condition): good (O), acceptable (H32, H34, H111) | |
Metal
- AA Grade 5456 O Aluminum Standard – Key Mechanical Properties
- AA Standards Grade 5454 H24 – Comprehensive Mechanical & Physical Properties
- AA 5083-O Aluminum Alloy Standard – High Strength & Corrosion Resistance
- AA Standards Grade 5454 H22 – Comprehensive Material Properties & Specifications
- AA Standards Grade 6066 T6 Aluminium Alloy Specifications
- AA 6351 T6 Aluminium Alloy – Technical Standards & Properties
- AA Standards Grade 5454 H111 – Comprehensive Mechanical Properties
- AA Standards Grade 5454 H112 – Aluminium Alloy Specifications
- AA Standards Grade 5454 H34: Comprehensive Mechanical Properties and Standards
- AA 5454 H32 – Standard Aluminium Grade & Properties