AA 3004 H32: Key Mechanical & Physical Properties
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.72 g/cm³ | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 105.0 MPa | H32 | AA Standards | |
Elastic modulus | 69.0 GPa | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
Hardness, Brinell | 52.0 [-] | H32 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||
Shear modulus | 25.0 - 26.0 GPa | Typical for Wrought 3000 Series Aluminium | ||
Tensile strength | 190.0 - 240.0 MPa | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
215.0 MPa | H32 | AA Standards |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3899999999999998e-05 1/K | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
100 °C | 2.3899999999999998e-05 1/K | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | ||
Melting point | 630.0 - 655.0 °C | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | ||
Specific heat capacity | 893.0 - 920.0 J/(kg·K) | Typical for Wrought 3000 Series Aluminium | |||
Thermal conductivity | 163 W/(m·K) | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 24000000.0 S/m | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Electrical resistivity | 4.17e-08 Ω·m | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Copper | 0.25 % | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Iron | 0.70 % | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Magnesium | 0.8 - 1.3 % | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Manganese | 1.0 - 1.5 % | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Silicon | 0.3 % | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Zinc | 0.25 % | H32 | AA Standards, ASTM B209, ASTM B313, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |
Metal
- AA Standards Grade 3004 H19 – Complete Material Property Overview
- AA Standards Grade 5056 H32 – Comprehensive Technical Overview
- AA Standards for Grade 3004 H26 Aluminium: Key Properties & Performance
- AA 3004 H34 Aluminum Alloy: Comprehensive Standards & Specifications
- AA Standards Grade 3004 H36: Technical Specifications & Mechanical Properties
- AA Standards Grade 3004 O: Comprehensive Properties & Performance Overview
- AA Standard Grade 5050 (H32): Specifications & Performance
- AA 5154 H32 Aluminium Standard – Key Properties & Compliance
- AA 5086 H32 Aluminum Alloy – Premium Strength & Corrosion Resistance for Structural Applications
- AA 5052 H32 Aluminum Alloy – Superior Corrosion Resistance & Welding Performance