EN 573-3 Grade 3.2315 T451 – Premium Structural Steel for High-Performance Engineering
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.7 g/cm³ | T451 | EN 573-3, EN 485 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending angle 180° | 3.0 °/t | T451 | EN 573-3, EN 485 | |
Bending angle 90° | 1.5 °/t | T451 | EN 573-3, EN 485 | |
2.0 °/t | T451 | EN 573-3, EN 485 | ||
3.0 °/t | T451 | EN 573-3, EN 485 | ||
4.0 °/t | T451 | EN 573-3, EN 485 | ||
Elastic modulus | 70.0 GPa | T451 | EN 573-3, EN 485 | |
Hardness, Brinell | 58.0 [-] | T451 | EN 573-3, EN 485 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Shear modulus | 26.4 GPa | T451 | EN 573-3, EN 485 | |
Tensile strength | 205.0 MPa | T451 | EN 573-3, EN 485 |
Thermal
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3399999999999996e-05 1/K | T451 | EN 573-3, EN 485 |
100 °C | 2.3399999999999996e-05 1/K | T451 | EN 573-3, EN 485 | |
Melting point | 585.0 - 650.0 °C | T451 | EN 573-3, EN 485 | |
Specific heat capacity | 896.0 J/(kg·K) | T451 | EN 573-3, EN 485 | |
Thermal conductivity | 170.0 - 220.0 W/(m·K) | T451 | EN 573-3, EN 485 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 24000000.0 - 32000000.0 S/m | T451 | EN 573-3, EN 485 |
Electrical resistivity | 3.13e-08 - 4.17e-08 Ω·m | T451 | EN 573-3, EN 485 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.25 % | T451 | EN 573-3, EN 485 |
Copper | 0.1 % | T451 | EN 573-3, EN 485 |
Iron | 0.50 % | T451 | EN 573-3, EN 485 |
Magnesium | 0.6 - 1.2 % | T451 | EN 573-3, EN 485 |
Manganese | 0.4 - 1.0 % | T451 | EN 573-3, EN 485 |
Silicon | 0.7 - 1.3 % | T451 | EN 573-3, EN 485 |
Titanium | 0.1 % | T451 | EN 573-3, EN 485 |
Zinc | 0.2 % | T451 | EN 573-3, EN 485 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: acceptable, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): good / sufficient, friction soldering: good, soft brazing with flux: acceptable | |
| Corrosion properties | Seawater: good, weathering: very good | |
| Workability | Bending / Spinning (cold): acceptable (T3, T4) / good (O), Impact extrusion (cold): good (O), Deep drawing / upsetting (Condition) good (O) / good (O) | |
Metal
- EN 573-3 Grade 3.2315 O3 Aluminium Alloy – Key Properties & Standards
- EN 573-3 Grade 3.2315 T39 Aluminium Alloy – Key Mechanical Properties
- EN 573-3 Grade 3.2315 (T89) - Technical Specifications & Properties
- EN 573-3 Grade 3.2315 F – Aluminium Alloy Specifications & Properties
- H13 Grade 3.2315 Steel – EN 573-3 Specification
- EN 573-3 Grade 3.2315 H18 – Aluminum 6000 Series Properties
- EN 573-3 Grade 3.2315 H111 – Detailed Aluminium Alloy Specifications
- EN 573-3 Grade 3.4335 T451 Aluminium: Specifications & Mechanical Properties
- EN 573-3 Grade 3.2315 T5 Aluminium: Key Mechanical Properties & Standards
- EN 573-3 Grade 3.2315 T42: Premium Aluminium with Superior Mechanical Properties