AA 5652 H32 Aluminium Grade – Standard Properties & Mechanical Data
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.67 g/cm³ | H32 | AA Standards, ASTM B209 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 115.0 MPa | H32 | AA Standards | |
Elastic modulus | 70.0 GPa | H32 | AA Standards, ASTM B209 | |
Hardness, Brinell | 60.0 [-] | H32 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Tensile strength | 215.0 - 265.0 MPa | H32 | AA Standards, ASTM B209 | |
230.0 MPa | H32 | AA Standards |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.38e-05 1/K | H32 | AA Standards, ASTM B209 | |
100 °C | 2.38e-05 1/K | H32 | AA Standards, ASTM B209 | ||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 605.0 - 650.0 °C | H32 | AA Standards, ASTM B209 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 138 W/(m·K) | H32 | AA Standards, ASTM B209 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 20000000.0 S/m | H32 | AA Standards, ASTM B209 |
Electrical resistivity | 5e-08 Ω·m | H32 | AA Standards, ASTM B209 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.15 - 0.35 % | H32 | AA Standards, ASTM B209 |
Copper | 0.04 % | H32 | AA Standards, ASTM B209 |
Magnesium | 2.2 - 2.8 % | H32 | AA Standards, ASTM B209 |
Manganese | 0.01 % | H32 | AA Standards, ASTM B209 |
Zinc | 0.1 % | H32 | AA Standards, ASTM B209 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: limited brazing | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |
Metal
- AA Standards Grade 5056 H32 – Comprehensive Technical Overview
- AA Standards Grade 5652 H22 – Full Mechanical & Physical Property Profile
- AA Standards Grade 5652 H24: Key Mechanical Properties & Specifications
- AA Standards Grade 5652 H112 – Comprehensive Mechanical Properties & Performance Overview
- AA Standards Grade 5456 H32 Aluminium: Key Mechanical & Physical Properties
- AA 5454 H32 – Standard Aluminium Grade & Properties
- AA Standards: Grade 5083 H32 Aluminium Alloy Specifications
- AA Standards Grade 5652 H38: Comprehensive Material Specifications
- AA 5652 O Aluminium Grade – Key Mechanical Properties & Standards
- AA Standard Grade 5254 H32 Aluminium Alloy Specifications