UGIMA® 4057 Tempered: Superior Machinability Martensitic Stainless Steel

UGIMA® 4057 is a member of the UGIMA® family of improved machinability martensitic stainless steels. It is developed exclusively by Ugitech. Its properties are identical to those of 1.4057, except for its machinability which is even better than that of 1.4057:

UGIMA® 4057’s new technological advances are extremely advantageous and a great improvement on 1.4057.

productivity increases of between 10% and 20% over grade 1.4057 have been obtained. Such increases are more noticeable in the case of monobloc carbide drilling or when a carbide-tipped toolbit is used.

In addition to excellent corrosion resistance, this stainless steel has the particular advantage of offering a wide range of mechanical properties in the processed condition. This grade also meets the requirements of EN10272 with respect to pressure vessels. Its performance - depending on its metallurgical condition - ensures compliance with high mechanical strength require-ments and meets the demands of applications where substantial resilience is needed.

Properties

General

Property	Value
Density	7.7 g/cm³

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23 °C	215 GPa
	100 °C	215 GPa
Elongation		15 %
Hardness, Brinell		321.0	max.
Reduction of area		45.0 %
Tensile strength		795 MPa	min.

Thermal

Property	Value	Comment
Coefficient of thermal expansion	0.0000105 1/K	20 to 100°C
Specific heat capacity	460 J/(kg·K)
Thermal conductivity	25 W/(m·K)

Electrical

Property	Value
Electrical resistivity	7e-07 Ω·m

Chemical properties

Property	Value	Comment
Carbon	0.16 - 0.2 %
Chromium	15.5 - 17.0 %
Manganese	1.0	max.
Phosphorus	0.035	max.
Silicon	0.8	max.
Sulfur	0.015 - 0.03 %

Technological properties

Property

Application areas

Process and energy industry, Chemical industry, Oil and petrochemical industries, Household and electrical appliance industry, Automotive and transport industry, Arms industry

Corrosion properties

This alloy has excellent atmospheric corrosion resistance and is one of the standard martensitic grades best able to withstand corrosion in marine environments; only structurally hardened grades such as UGIMA® 4542 have a higher re-sistance (amongst martensitic grades).

UGIMA® 4057 is also resistant to certain petroleum and organic products.

Environment	Behaviour/ Use
Nitric acid	Good
Phosphoric acid	Restricted use
Sulphuric acid	Restricted use
Acetic acid	Restricted use
Sodium carbonate	Average
NaCl (Saline mist )	Average
Humidity	Good
Sea water	Restricted use

Note: The corrosion resistance of a stainless steel depends on many factors related to the composition of the corro-sive atmosphere (chloride concentration, presence or absence of oxidising agents, temperature, pH, agitation or no agi-tation, and so on), as well as to the preparation of the material (surfaces free from metal particles, surface finish, such as hardening, polishing, and so on).

Precautionary measures should be taken for certain tests such as the saline mist test (French standard NFX 41002), for example marking labels (that might cause corrosion run-outs and reduce the test resistance time) should not be used on the test pieces.

In terms of pitting corrosion UGIMA® 4057 performs better than most martensiitic grades.

Hot forming

Forging: UGIMA® 4057 is suitable for forging. It is heated slowly to 850°C, then more quickly to 1150/1180°C for forging be-tween 1180°C and 950°C. Forging must be followed by a stress relief heat treatment at 200°C or softening at between 750 and 850°C or hardening and tempering

Other

Available products:

Product	Shape	Finish	Tolerance	Dimensions
Bar	Round	Rolled and descaled bars	12 to 13	22 to 15 mm
		Turned and polished	9 to 11	22 to 115 mm
		Drawn bar	8 to 9	3 to 55 mm
		Ground bar	6 to 9	3 to 80 mm
		Drawn bar	11	3 to 55 mm
Wire rod	Round	Pickeled		5.0 to 32 mm
Drawn wire	Round			16.0 to 1.0 mm

weight:normal;overflow:hidden;padding:1px 2px;text-align:center;vertical-align:top;word-break:normal">Drawn wire

Round

16.0 to 1.0 mm

Welding

Provided certain precautionary measures are taken, UGIMA® 4057 can be subjected to most arc welding or resistance welding techniques in tempered, hardened or softened condition.

To prevent any risk of cold weld cracking, UGIMA® 4057 must be preheated to between 200 and 300°C and the temper-atures between passes maintained at a minimum of 200°C. A stress relief heat treatment at 650°C is also required after welding.

If a filler metal is needed, a wire with a similar composition to that of UGIMA® 4057, such as AWS E/ER410 is recom-mended. AWS E/ER310 austenitic wire can also be used if the mechanical properties on welding and the response of the welding to the post welding heat treatment are not required to be the same as those of the base metal.

Ar + 1 to 3% CO₂ or O₂ shielding gases are recommended for MIG welding. Gas containing H₂ should not be used. Coated electrodes must be oven dried before welding.Heat treatment