AW-2030 T3511 – Premium Age‑Hardenable AlCu Alloy (EN 573-3)
Age-hardenable AlCu alloy. The alloy is not food safe.
Properties
General
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Density | 2.81 g/cm³ | T3511 | EN 573-3, EN 754 | Rod, Tube |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 72.5 GPa | T3511 | EN 573-3, EN 754 | Rod, Tube | ||
Elongation | 3.0 % | T3511 | EN 573-3, EN 754 | Rod, Tube | A50 | |
5.0 % | T3511 | EN 573-3, EN 754 | Rod, Tube | A100 | ||
20.0 °C | 3.0 % | T3511 | EN 573-3 | Rod, Tube | A50 | |
20.0 °C | 5.0 % | T3511 | EN 573-3 | Rod, Tube | ||
Hardness, Brinell | 20.0 °C | 115.0 [-] | T3511 | EN 573-3 | Rod, Tube | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||||
Shear modulus | 27.2 GPa | T3511 | EN 573-3, EN 754 | Rod, Tube | ||
Tensile strength | 370.0 MPa | T3511 | EN 573-3, EN 754 | Rod, Tube | ||
20.0 °C | 370.0 MPa | T3511 | EN 573-3 | Rod, Tube |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Melting point | 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Specific heat capacity | 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Thermal conductivity | 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Bismuth | 0.2 % | T3511 | EN 573-3, EN 754 | Rod, Tube |
Chromium | 0.1 % | T3511 | EN 573-3, EN 754 | Rod, Tube |
Copper | 3.3 - 4.5 % | T3511 | EN 573-3, EN 754 | Rod, Tube |
Iron | 0.7 % | T3511 | EN 573-3 | Rod, Tube |
0.70 % | T3511 | EN 573-3, EN 754 | Rod, Tube | |
Lead | 0.8 - 1.5 % | T3511 | EN 573-3, EN 754 | Rod, Tube |
Magnesium | 0.5 - 1.3 % | T3511 | EN 573-3, EN 754 | Rod, Tube |
Manganese | 0.2 - 1.0 % | T3511 | EN 573-3, EN 754 | Rod, Tube |
Silicon | 0.8 % | T3511 | EN 573-3, EN 754 | Rod, Tube |
Titanium | 0.2 % | T3511 | EN 573-3, EN 754 | Rod, Tube |
Zinc | 0.5 % | T3511 | EN 573-3, EN 754 | Rod, Tube |
Technological properties
| Property | ||
|---|---|---|
| Workability | Moderate Workability | |
Metal
- EN 573-3 Grade 3.1325 T3511 – Comprehensive Material Properties & Standards
- EN 573-3 Grade 3.1645 T3511 Aluminium: Key Properties & Standards
- EN 573-3 Grade AW-2030 T351 Aluminum Alloy – Properties & Applications
- AW-2030 T3510 – Premium Age-Hardenable AlCu Alloy (EN 573-3)
- EN 573-3 AW-2030 T4510: Age-Hardenable High‑Strength Aluminum Alloy
- AW-2030 T4511 Aluminium Alloy – EN 573-3 Grade, Age‑Hardenable, High Strength
- AW-2030 T4 Aluminum Alloy – EN 573-3 Certified
- EN 573-3 AW-2030 T3 Aluminum Alloy – Density, Strength, Modulus & Elongation
- EN 573-3 Grade 3.1255 T3511 Aluminum Alloy – High Strength & Weldability
- EN 573-3 Grade 3.1355 T3511 Aluminum Alloy – High Strength for Aerospace Applications