AW-2011A T3 Aluminium Alloy – EN 573-3 Grade, High Strength Age-Hardenable Composition
Age-hardenable AlCu alloy. The alloy is not food safe.
Properties
General
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Density | 2.82 g/cm³ | T3 | EN 573-3, EN 754 | Rod, Tube |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 70.0 - 73.0 GPa | Typical for Wrought 2000 Series Aluminium | ||||
Elongation | 6.0 % | T3 | EN 573-3, EN 754 | Rod, Tube | A50 | |
8.0 % | T3 | EN 573-3, EN 754 | Rod, Tube | A50 | ||
8.0 % | T3 | EN 573-3, EN 754 | Rod, Tube | A100 | ||
10.0 % | T3 | EN 573-3, EN 754 | Rod, Tube | A100 | ||
20.0 °C | 6.0 % | T3 | EN 573-3 | Tube | A50 | |
20.0 °C | 8.0 % | T3 | EN 573-3 | Rod, Tube | A50 | |
20.0 °C | 8.0 % | T3 | EN 573-3 | Tube | ||
20.0 °C | 10.0 % | T3 | EN 573-3 | Rod, Tube | ||
Hardness, Brinell | 20.0 °C | 90.0 [-] | T3 | EN 573-3 | Rod, Tube | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||||
Shear modulus | 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||||
Tensile strength | 280.0 MPa | T3 | EN 573-3, EN 754 | Rod, Tube | ||
290.0 MPa | T3 | EN 573-3, EN 754 | Rod, Tube | |||
300.0 MPa | T3 | EN 573-3, EN 754 | Rod, Tube | |||
310.0 MPa | T3 | EN 573-3, EN 754 | Rod, Tube | |||
320.0 MPa | T3 | EN 573-3, EN 754 | Rod, Tube | |||
20.0 °C | 280.0 MPa | T3 | EN 573-3 | Rod | ||
20.0 °C | 290.0 MPa | T3 | EN 573-3 | Tube | ||
20.0 °C | 300.0 MPa | T3 | EN 573-3 | Rod | ||
20.0 °C | 310.0 MPa | T3 | EN 573-3 | Tube | ||
20.0 °C | 320.0 MPa | T3 | EN 573-3 | Rod |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Melting point | 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Specific heat capacity | 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Thermal conductivity | 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Bismuth | 0.2 - 0.6 % | T3 | EN 573-3, EN 754 | Rod, Tube |
Copper | 4.5 - 6.0 % | T3 | EN 573-3, EN 754 | Rod, Tube |
Iron | 0.5 % | T3 | EN 573-3 | Rod, Tube |
0.50 % | T3 | EN 573-3, EN 754 | Rod, Tube | |
Lead | 0.2 - 0.6 % | T3 | EN 573-3, EN 754 | Rod, Tube |
Silicon | 0.4 % | T3 | EN 573-3, EN 754 | Rod, Tube |
Zinc | 0.3 % | T3 | EN 573-3, EN 754 | Rod, Tube |
Technological properties
| Property | ||
|---|---|---|
| Workability | Moderate Workability | |
Metal
- EN 573-3 AW-8008 O – Food‑Safe, High‑Strength AlFeMn Alloy
- AW-4007 F Aluminum Alloy – EN 573-3 Certified, Food-Safe, High-Strength
- AW‑6951 O (EN 573‑3): Food‑Safe Age‑Hardenable AlMgSi Alloy
- AW-5040 O: Certified Food‑Safe Aluminium Alloy (EN 573‑3)
- AW-2618A T6 – Premium Age-Hardenable AlCu Alloy (EN 573-3 Grade)
- AW-6064A T8 Aluminium Alloy – EN 573-3 Certified Grade
- AW-6064A T9: EN 573-3 Certified Age-Hardenable AlMgSi Alloy
- EN 573-3 Grade AW-2011A T4 – High-Performance Age-Hardenable AlCu Alloy
- AW-2011A T6 Aluminium Alloy – EN 573-3 Grade Specifications
- EN 573-3 Grade AW-2011A T8 Aluminum Alloy – Properties & Standards