EN 573-3 Grade 3.3535 H111 – Premium Aluminum Alloy for Industrial Applications

Quantity: One truck load – Specialty products on request.Additional services: Via Cindal (the Aludium R&D department): R&D services, benchmarking, chemical audits, material specification, process optimisation, quality monitoring, sample analysis, prototyping, training

Properties

General

Property	Value	Condition	Related Standards
Density	2.66 g/cm³	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755

Mechanical

Property	Value	Condition	Related Standards	Comment
Bending angle 180°	0.5 °/t	H111	EN 573-3, EN 485
	1.0 °/t	H111	EN 573-3, EN 14286, EN 485
	2.0 °/t	H111	EN 573-3, EN 14286
Bending angle 90°	0.5 °/t	H111	EN 573-3, EN 485
	1.0 °/t	H111	EN 573-3, EN 485
	2.0 °/t	H111	EN 573-3, EN 485
Elastic modulus	70.5 GPa	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Hardness, Brinell	52.0 [-]	H111	EN 573-3, EN 485
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 5000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 5000 Series Aluminium
Shear modulus	26.5 GPa	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Tensile strength	180.0 - 250.0 MPa	H111	EN 573-3, EN 754, EN 755
	190.0 - 240.0 MPa	H111	EN 573-3, EN 14286, EN 485

Thermal

Property	Temperature	Value	Condition	Related Standards	Comment
Coefficient of thermal expansion	20 °C	2.3899999999999998e-05 1/K	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
	100 °C	2.3899999999999998e-05 1/K	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Max service temperature		150.0 °C			Typical for Wrought 5000 Series Aluminium
Melting point		610.0 - 640.0 °C	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Specific heat capacity		879.0 - 963.0 J/(kg·K)			Typical for Wrought 5000 Series Aluminium
Thermal conductivity		140.0 - 160.0 W/(m·K)	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	20000000.0 - 23000000.0 S/m	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Electrical resistivity	4.35e-08 - 5e-08 Ω·m	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755

Chemical properties

Property	Value	Condition	Related Standards
Copper	0.1 %	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Iron	0.40 %	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Magnesium	2.6 - 3.6 %	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Manganese	0.5 %	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Silicon	0.4 %	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Titanium	0.15 %	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Zinc	0.2 %	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755

Technological properties

Property
Anodizing	decorative: gut (EQ: sehr gut), Protective: very good
Brazing	hard brazing (with flux/ without flux): poor / sufficient, friction soldering: acceptable, soft brazing with flux: poor
Corrosion properties	Seawater: very good to good, weathering: very good
Workability	Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): sufficient, Deep drawing / upsetting (Condition) good (O) / good (H12)

EN 573-3 Grade 3.3527 H34: Comprehensive Material Properties & Standards EN 573-3 Grade 3.3535 H38 – Premium Stainless Steel for Heavy‑Duty Use

Metal