EN 1706 Grade AC-46100 F Aluminium Casting Alloy
Aluminium casting alloy (pressure die casting)
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.65 - 2.7 g/cm³ | Typical for Cast 3xx.x Series Aluminium |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending Fatigue Strength | 60.0 - 90.0 MPa | F | EN 1706 | Casting | ||
Elastic modulus | 73.0 - 80.0 GPa | Typical for Cast 3xx.x Series Aluminium | ||||
Hardness, Brinell | 80.0 [-] | F | EN 1706 | Casting | ||
20.0 °C | 80.0 [-] | F | EN 1706 | |||
Poisson's ratio | 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | ||||
Shear modulus | 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | ||||
Tensile strength | 240.0 MPa | F | EN 1706 | Casting | ||
20.0 °C | 240.0 MPa | F | EN 1706 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 1.9999999999999998e-05 1/K | F | EN 1706 | Casting | |
100 °C | 1.9999999999999998e-05 1/K | F | EN 1706 | Casting | ||
100.0 °C | 2e-05 1/K | F | EN 1706 | |||
Melting point | 505.0 - 770.0 °C | Typical for Cast 3xx.x Series Aluminium | ||||
Specific heat capacity | 960.0 - 963.0 J/(kg·K) | Typical for Cast 3xx.x Series Aluminium | ||||
Thermal conductivity | 20.0 °C | 120.0 - 130.0 W/(m·K) | F | EN 1706 | Casting |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 14000000.0 - 18000000.0 S/m | F | EN 1706 | Casting |
Electrical resistivity | 5.56e-08 - 7.14e-08 Ω·m | F | EN 1706 | Casting |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Aluminium | 80.25 % | F | EN 1706 | |
Chromium | 0.15 % | F | EN 1706 | Casting |
Copper | 1.5 - 2.5 % | F | EN 1706 | Casting |
Iron | 1.1 % | F | EN 1706 | |
1.10 % | F | EN 1706 | Casting | |
Lead | 0.25 % | F | EN 1706 | Casting |
Magnesium | 0.3 % | F | EN 1706 | Casting |
Manganese | 0.55 % | F | EN 1706 | Casting |
Nickel | 0.45 % | F | EN 1706 | Casting |
Silicon | 10.0 - 12.0 % | F | EN 1706 | Casting |
Tin | 0.25 % | F | EN 1706 | Casting |
Titanium | 0.25 % | F | EN 1706 | Casting |
Zinc | 1.7 % | F | EN 1706 | Casting |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: not recommended | |
| Corrosion properties | general: not sufficient | |
| General machinability | after thermal treatment: acceptable | |
| Processing methods | pressure die casting, separately cast test sample | |
Metal
- EN 1706 AC-44000 F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 Grade AC-44100 F – High-Performance Aluminium Casting Alloy
- EN 1706 Grade AC-44200 F Aluminium Casting Alloy – High-Performance, Industrial Grade
- EN 1706 AC-44300 F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 AC-44400F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 AC-51200 F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 Grade AC-51300 F – High-Strength Aluminium Casting Alloy
- EN 1706 AC-46500 F – Aluminium Die Casting Alloy: Properties & Standards
- EN 1706 AC‑46600 F Aluminium Alloy – High‑Strength, Low‑Density Casting Solution
- EN 1706 AC-47000 F Aluminium Casting Alloy – Specifications