EN 573-3 Grade 3.1255 (T4510) – High-Performance Aluminum Alloy

DIN 3.1255 is an alloy with strength, machinability and welding capabilities, Aluminum Alloy DIN 3.1255 is an excellent option. It is a precipitation hardening alloy that maintains strength after heat treatment.

Properties

General

Property	Value	Condition	Related Standards
Density	2.8 g/cm³	T4510	EN 573-3, EN 754, EN 755

Mechanical

Property	Value	Condition	Related Standards	Comment
Elastic modulus	73.0 GPa	T4510	EN 573-3, EN 754, EN 755
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 2000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 2000 Series Aluminium
Shear modulus	27.4 GPa	T4510	EN 573-3, EN 754, EN 755
Tensile strength	350.0 MPa	T4510	EN 573-3, EN 755
	370.0 MPa	T4510	EN 573-3, EN 755
	380.0 MPa	T4510	EN 573-3, EN 754
	390.0 MPa	T4510	EN 573-3, EN 755
	410.0 MPa	T4510	EN 573-3, EN 755

Thermal

Property	Temperature	Value	Condition	Related Standards	Comment
Coefficient of thermal expansion	-50 °C	2.1e-05 1/K	T4510	EN 573-3, EN 754, EN 755
	20 °C	2.1e-05 1/K	T4510	EN 573-3, EN 754, EN 755
	20 °C	2.28e-05 1/K	T4510	EN 573-3, EN 754, EN 755
	20 °C	2.3e-05 1/K	T4510	EN 573-3, EN 754, EN 755
	20 °C	2.36e-05 1/K	T4510	EN 573-3, EN 754, EN 755
	20 °C	2.46e-05 1/K	T4510	EN 573-3, EN 754, EN 755
	100 °C	2.28e-05 1/K	T4510	EN 573-3, EN 754, EN 755
	100 °C	2.3e-05 1/K	T4510	EN 573-3, EN 754, EN 755
	200 °C	2.36e-05 1/K	T4510	EN 573-3, EN 754, EN 755
	300 °C	2.46e-05 1/K	T4510	EN 573-3, EN 754, EN 755
Melting point		505.0 - 635.0 °C	T4510	EN 573-3, EN 754, EN 755
		510.0 - 640.0 °C	T4510	EN 573-3, EN 754, EN 755
Specific heat capacity		816.0 - 963.0 J/(kg·K)			Typical for Wrought 2000 Series Aluminium
Thermal conductivity		134.0 - 193.0 W/(m·K)	T4510	EN 573-3, EN 754, EN 755
		140.0 - 200.0 W/(m·K)	T4510	EN 573-3, EN 754, EN 755

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	20000000.0 - 29000000.0 S/m	T4510	EN 573-3, EN 754, EN 755
	21000000.0 - 24000000.0 S/m	T4510	EN 573-3, EN 754, EN 755
Electrical resistivity	3.45e-08 - 5e-08 Ω·m	T4510	EN 573-3, EN 754, EN 755
	4.17e-08 - 4.76e-08 Ω·m	T4510	EN 573-3, EN 754, EN 755

Chemical properties

Property	Value	Condition	Related Standards
Chromium	0.1 %	T4510	EN 573-3, EN 754, EN 755
Copper	3.9 - 5.0 %	T4510	EN 573-3, EN 754, EN 755
Iron	0.70 %	T4510	EN 573-3, EN 754, EN 755
Magnesium	0.2 - 0.8 %	T4510	EN 573-3, EN 754, EN 755
Manganese	0.4 - 1.2 %	T4510	EN 573-3, EN 754, EN 755
Silicon	0.5 - 1.2 %	T4510	EN 573-3, EN 754, EN 755
Titanium	0.15 %	T4510	EN 573-3, EN 754, EN 755
Zinc	0.25 %	T4510	EN 573-3, EN 754, EN 755

Technological properties

Property
Anodizing	decorative: not suitable, Protective: acceptable
Brazing	hard brazing (with flux/ without flux): not suitable / not suitable, friction soldering: acceptable, soft brazing with flux: not suitable
Corrosion properties	Seawater: sufficient, weathering: acceptable
Workability	Bending / Spinning (cold): gut (O) / ungeeignet, Impact extrusion (cold): not suitable, Deep drawing / upsetting (Condition) acceptable (O) / not suitable

EN 573-3 Grade 3.1255 T3511 Aluminum Alloy – High Strength & Weldability EN 573-3 Grade 3.1255 T4511: High‑Strength, Heat‑Treated Aluminum Alloy

Metal