AA 7075 T62 Aluminum Alloy – Premium Strength for Aerospace Applications
AA 7075 is a high-strength alloy that offers good stress-corrosion cracking resistance. Known as a mainstay in the aerospace industry since it was introduced, Aluminum 7075 brings moderate toughness as well as an excellent strength-to-weight ratio. It is also important to note that at sub-zero temperatures Aluminum 7075 increases in strength.
Additional services: Cuttings, Parts from drawingsSTEEL SCOUT
DISTRIBUTOR
Information and services
Quantity: 1 PCSProperties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.7 - 2.85 g/cm³ | Typical for Wrought 7000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 69.0 - 72.0 GPa | Typical for Wrought 7000 Series Aluminium | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 7000 Series Aluminium | ||
Shear modulus | 26.4 - 27.1 GPa | Typical for Wrought 7000 Series Aluminium | ||
Tensile strength | 460.0 MPa | T62 | AA Standards, ASTM B209 | |
490.0 MPa | T62 | AA Standards, ASTM B209 | ||
495.0 MPa | T62 | AA Standards, ASTM B209 | ||
510.0 MPa | T62 | AA Standards, ASTM B209 | ||
525.0 MPa | T62 | AA Standards, ASTM B209 | ||
530.0 MPa | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211 | ||
540.0 MPa | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | ||
560.0 MPa | T62 | AA Standards, ASTM B221, ASTM B241 |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.1e-05 - 2.4e-05 1/K | Typical for Wrought 7000 Series Aluminium |
Melting point | 465.0 - 655.0 °C | Typical for Wrought 7000 Series Aluminium |
Specific heat capacity | 795.0 - 1050.0 J/(kg·K) | Typical for Wrought 7000 Series Aluminium |
Thermal conductivity | 121.0 - 170.0 W/(m·K) | Typical for Wrought 7000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 34000000.0 S/m | Typical for Wrought 7000 Series Aluminium |
Electrical resistivity | 2.9e-08 - 5.6e-08 Ω·m | Typical for Wrought 7000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.18 - 0.28 % | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241 |
Copper | 1.2 - 2.0 % | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241 |
Iron | 0.50 % | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241 |
Magnesium | 2.1 - 2.9 % | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241 |
Manganese | 0.3 % | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241 |
Silicon | 0.4 % | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241 |
Titanium | 0.2 % | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241 |
Zinc | 5.1 - 6.1 % | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O), good to acceptable | |
| Workability | general (condition): not suitable | |
Metal
- High-Strength AA 7075 H13 Aluminum Alloy – Aerospace Grade
- AA 7075 T3510 – High-Strength Aluminum Alloy for Aerospace Applications
- High-Strength AA 7075 Grade T3511 – Premium Aerospace Alloy
- High-Strength AA 7075 Aluminum Alloy – Grade 7075 T73511
- High‑Strength AA 7075 T7352 Alloy – Aerospace Grade Aluminum
- AA 7075 T76: High‑Strength Aerospace Grade Aluminum Alloy
- AA 7075 T7651 – Premium High‑Strength Aluminum Alloy for Aerospace
- AA 7075 T6 – Premium High-Strength Aluminum Alloy for Aerospace
- AA 7075 T76510: Premium High-Strength Aluminum Alloy
- High-Strength AA 7075 Alloy – Superior Aerospace Grade