EN 573-3 AW-6016 T6 Aluminium Alloy – Age‑Hardenable, Food Safe, High Strength
Age-hardenable AlMgSi alloy. The alloy is food safe.
Properties
General
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Density | 2.7 g/cm³ | T6 | EN 573-3, EN 485 | Strip, Sheet, Plate |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 70.0 GPa | Typical for Wrought 6000 Series Aluminium | ||||
Hardness, Brinell | 80.0 [-] | T6 | EN 573-3, EN 485 | Strip, Sheet, Plate | ||
20.0 °C | 80.0 [-] | T6 | EN 573-3 | Flat | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||||
Tensile strength | 20.0 °C | 260.0 - 300.0 MPa | T6 | EN 573-3 | Flat | Transverse |
20.0 °C | 260.0 - 300.0 MPa | T6 | EN 573-3, EN 485 | Flat, Strip, Sheet, Plate |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 6000 Series Aluminium |
Melting point | 555.0 - 655.0 °C | Typical for Wrought 6000 Series Aluminium |
Specific heat capacity | 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium |
Thermal conductivity | 170.0 - 220.0 W/(m·K) | Typical for Wrought 6000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 21000000.0 - 34000000.0 S/m | Typical for Wrought 6000 Series Aluminium |
Electrical resistivity | 2.9e-08 - 5e-08 Ω·m | Typical for Wrought 6000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 % | T6 | EN 573-3, EN 485 | Flat, Strip, Sheet, Plate |
Copper | 0.2 % | T6 | EN 573-3, EN 485 | Flat, Strip, Sheet, Plate |
Iron | 0.5 % | T6 | EN 573-3 | Flat |
0.50 % | T6 | EN 573-3, EN 485 | Strip, Sheet, Plate | |
Magnesium | 0.25 - 0.6 % | T6 | EN 573-3, EN 485 | Flat, Strip, Sheet, Plate |
Manganese | 0.2 % | T6 | EN 573-3, EN 485 | Flat, Strip, Sheet, Plate |
Silicon | 1.0 - 1.5 % | T6 | EN 573-3, EN 485 | Flat, Strip, Sheet, Plate |
Titanium | 0.15 % | T6 | EN 573-3, EN 485 | Flat, Strip, Sheet, Plate |
Zinc | 0.2 % | T6 | EN 573-3, EN 485 | Flat, Strip, Sheet, Plate |
Technological properties
| Property | ||
|---|---|---|
| Workability | Excellent workability. | |
Metal
- EN 573-3 Grade 3.0505 F Aluminium Alloy: Properties & Standards
- EN 573-3 Grade 3.1305 F Aluminium Alloy – Key Mechanical Properties
- EN 573-3 Grade 3.1305 O Aluminium: Key Mechanical Properties & Standards
- EN 573-3 Grade 3.1305 O3 – Comprehensive Aluminium Alloy Specifications
- EN 573-3 Grade 3.3316 F – Key Properties & Standards for 5000 Series Aluminium
- EN 573-3 Grade 3.3549 F – Premium Aluminum Alloy with Expert R&D Support
- EN 573-3 AW‑1090 F Aluminium: Technical Specifications & Standards
- AW-5356 F Aluminum Alloy – EN 573‑3 Specification & Key Mechanical Properties
- EN 573-3 Grade AW-5356 O3 Aluminium Alloy – Key Properties & Standards
- AW-5183 O3 Aluminium Alloy – EN 573-3 Grade & Key Properties