EN 573-3 Grade 3.3547 H32 – Comprehensive Material Properties & Standards
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.66 g/cm³ | H32 | EN 573-3, EN 485, EN 754 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 140.0 MPa | H32 | EN 573-3, EN 485, EN 754 | |
Bending angle 180° | 2.0 °/t | H32 | EN 573-3, EN 485 | |
3.0 °/t | H32 | EN 573-3, EN 485 | ||
Bending angle 90° | 0.5 °/t | H32 | EN 573-3, EN 485 | |
1.5 °/t | H32 | EN 573-3, EN 485 | ||
2.0 °/t | H32 | EN 573-3, EN 485 | ||
2.5 °/t | H32 | EN 573-3, EN 485 | ||
3.5 °/t | H32 | EN 573-3, EN 485 | ||
Elastic modulus | 71.0 GPa | H32 | EN 573-3, EN 485, EN 754 | |
Hardness, Brinell | 89.0 [-] | H32 | EN 573-3, EN 485 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.8 GPa | H32 | EN 573-3, EN 485, EN 754 | |
Tensile strength | 280.0 MPa | H32 | EN 573-3, EN 754 | |
305.0 - 380.0 MPa | H32 | EN 573-3, EN 485 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | -50 °C | 2.23e-05 1/K | H32 | EN 573-3, EN 485, EN 754 | |
20 °C | 2.23e-05 1/K | H32 | EN 573-3, EN 485, EN 754 | ||
20 °C | 2.42e-05 1/K | H32 | EN 573-3, EN 485, EN 754 | ||
20 °C | 2.4999999999999998e-05 1/K | H32 | EN 573-3, EN 485, EN 754 | ||
20 °C | 2.6e-05 1/K | H32 | EN 573-3, EN 485, EN 754 | ||
100 °C | 2.42e-05 1/K | H32 | EN 573-3, EN 485, EN 754 | ||
200 °C | 2.4999999999999998e-05 1/K | H32 | EN 573-3, EN 485, EN 754 | ||
300 °C | 2.6e-05 1/K | H32 | EN 573-3, EN 485, EN 754 | ||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 574.0 - 638.0 °C | H32 | EN 573-3, EN 485, EN 754 | ||
Specific heat capacity | 900.0 J/(kg·K) | H32 | EN 573-3, EN 485, EN 754 | ||
Thermal conductivity | 110.0 - 140.0 W/(m·K) | H32 | EN 573-3, EN 485, EN 754 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 16000000.0 - 19000000.0 S/m | H32 | EN 573-3, EN 485, EN 754 |
Electrical resistivity | 5.26e-08 - 6.25e-08 Ω·m | H32 | EN 573-3, EN 485, EN 754 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.05 - 0.25 % | H32 | EN 573-3, EN 485, EN 754 |
Copper | 0.1 % | H32 | EN 573-3, EN 485, EN 754 |
Iron | 0.40 % | H32 | EN 573-3, EN 485, EN 754 |
Magnesium | 4.0 - 4.9 % | H32 | EN 573-3, EN 485, EN 754 |
Manganese | 0.4 - 1.0 % | H32 | EN 573-3, EN 485, EN 754 |
Silicon | 0.4 % | H32 | EN 573-3, EN 485, EN 754 |
Titanium | 0.15 % | H32 | EN 573-3, EN 485, EN 754 |
Zinc | 0.25 % | H32 | EN 573-3, EN 485, EN 754 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: sufficient, Protective: good | |
| Brazing | hard brazing (with flux/ without flux): poor / poor, friction soldering: acceptable, soft brazing with flux: poor | |
| Corrosion properties | Seawater: very good, weathering: very good | |
| Workability | Bending / Spinning (cold): good / sufficient, Impact extrusion (cold): sufficient, Deep drawing / upsetting (Condition) good (O) / good (O) | |
Metal
- EN 573-3 Grade 3.3316 H32 – Specifications & Mechanical Properties
- EN 573-3 Grade 3.3547 H28 Aluminum – Key Properties & Standards
- EN 573-3 Grade 3.3547 H38 – High-Strength Aluminium Alloy Properties
- EN 573-3 Grade 3.3315 H32: Key Mechanical Properties & Standards
- EN 573-3 Grade 3.3547 H16 Aluminium: Key Mechanical Properties & Standards
- EN 573-3 Grade 3.3547 H26 Aluminium: Key Properties & Standards
- EN 573-3 Grade 3.3547 H36 Aluminium: Key Mechanical Properties & Standards
- EN 573-3 Grade 3.3547 H112 Aluminium - Key Properties & Standards
- EN 573-3 Grade 3.3547 H114 – Aluminium Alloy Properties & Standards
- EN 573-3 Grade 3.3547 H224 – Certified Aluminium Alloy Properties