AA 5005 H24 Aluminum Alloy – Low Density, Corrosion‑Resistant, and Thermally Conductive
Aluminum AA 5005 is a lean aluminum magnesium alloy with low density and excellent thermal conductivity. This medium strength non-heat-treatable alloy is known for its corrosion resistance in alkaline marine situations. Aluminum AA 5005 is readily machinable, and can be welded using TIG and MIG methods. It is important to note that anodizing is a critical part to how Aluminum AA 5005 is used.
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.7 g/cm³ | H24 | AA Standards, ASTM B209 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 69.0 GPa | H24 | AA Standards, ASTM B209 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Tensile strength | 140.0 - 180.0 MPa | H24 | AA Standards, ASTM B209 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.38e-05 1/K | H24 | AA Standards, ASTM B209 | |
100 °C | 2.38e-05 1/K | H24 | AA Standards, ASTM B209 | ||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 630.0 - 655.0 °C | H24 | AA Standards, ASTM B209 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 201 W/(m·K) | H24 | AA Standards, ASTM B209 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 30000000.0 S/m | H24 | AA Standards, ASTM B209 |
Electrical resistivity | 3.33e-08 Ω·m | H24 | AA Standards, ASTM B209 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.1 % | H24 | AA Standards, ASTM B209 |
Copper | 0.2 % | H24 | AA Standards, ASTM B209 |
Iron | 0.70 % | H24 | AA Standards, ASTM B209 |
Magnesium | 0.5 - 1.1 % | H24 | AA Standards, ASTM B209 |
Manganese | 0.2 % | H24 | AA Standards, ASTM B209 |
Silicon | 0.3 % | H24 | AA Standards, ASTM B209 |
Zinc | 0.25 % | H24 | AA Standards, ASTM B209 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12, H32), poor (H14, H34, H16, H18, H36, H38) | |
| Workability | general (condition): good (O, H12, H32), acceptable (H14, H34), poor(H16, H18, H36, H38) | |
Metal
- AA Grade 5010 H24 – Key Mechanical Properties & Standards
- AA Standards Grade 8176 H24 – Comprehensive Aluminium Alloy Specs
- AA Standard Grade 3105 H24 – Key Mechanical Properties & Specifications
- AA Standards Grade 1060 H24 – Properties & Specifications
- AA 3004 H24 Aluminum Alloy: Grade, Properties, and Standards
- AA Standards Grade 5050 H24 – Comprehensive Aluminium Property Profile
- AA Standards Grade 5254 H24 – Detailed Mechanical & Physical Properties
- AA Standards Grade 5457 H24: Key Mechanical & Physical Properties
- AA Standards Grade 5454 H24 – Comprehensive Mechanical & Physical Properties
- AA Standards Grade 5154 H24 – Aluminium Properties & Specifications