AA 5052 H22 Aluminum Alloy – Superior Corrosion Resistance & Weldability
Aluminum AA 5052 is a non-heat treatable alloy with excellent finishing qualities. AA 5052 offers better corrosion resistance than most aluminum alloys, especially to salt water and marine atmospheres. This alloy can be readily welded using most common techniques and is in fact offers some of the best welding characteristics of all aluminum alloys.
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.68 g/cm³ | H22 | AA Standards, ASTM B209 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 70.0 GPa | H22 | AA Standards, ASTM B209 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Tensile strength | 215.0 - 265.0 MPa | H22 | AA Standards, ASTM B209 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.38e-05 1/K | H22 | AA Standards, ASTM B209 | |
100 °C | 2.38e-05 1/K | H22 | AA Standards, ASTM B209 | ||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 605.0 - 650.0 °C | H22 | AA Standards, ASTM B209 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 138 W/(m·K) | H22 | AA Standards, ASTM B209 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 20000000.0 S/m | H22 | AA Standards, ASTM B209 |
Electrical resistivity | 5e-08 Ω·m | H22 | AA Standards, ASTM B209 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.15 - 0.35 % | H22 | AA Standards, ASTM B209 |
Copper | 0.1 % | H22 | AA Standards, ASTM B209 |
Iron | 0.40 % | H22 | AA Standards, ASTM B209 |
Magnesium | 2.2 - 2.8 % | H22 | AA Standards, ASTM B209 |
Manganese | 0.1 % | H22 | AA Standards, ASTM B209 |
Silicon | 0.25 % | H22 | AA Standards, ASTM B209 |
Zinc | 0.1 % | H22 | AA Standards, ASTM B209 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: limited brazing | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |
Metal
- AA Standards Grade 5010 H22: Key Mechanical Properties & Compliance
- AA Standards Grade 3105 H22: Comprehensive Property Overview
- AA 1060 H22 Aluminium Alloy – Full Grade Specifications & Mechanical Properties
- AA Standard 3004 H22: Comprehensive Mechanical Properties & Specifications
- AA Standards Grade 5050 H22: Key Mechanical and Physical Properties
- AA 5154 H22 – 5000 Series Aluminum: Standards, Mechanical Properties & Key Specifications
- AA Standards Grade 5652 H22 – Full Mechanical & Physical Property Profile
- AA Standards Grade 5454 H22 – Comprehensive Material Properties & Specifications
- AA Standards 5254 H22 – Technical Specifications for Aluminium Alloy
- AA 5052 H28 Aluminum Alloy – Superior Corrosion Resistance & Weldability