EN 573-3 AW‑7010 T652: Premium Age‑Hardening Aluminum Alloy
Age-hardenable AlZn alloy. The alloy is not food safe.
Properties
General
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Density | 2.82 g/cm³ | T652 | EN 573-3, EN 485 | Strip, Sheet, Plate |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending angle 90° | 12.0 °/t | T652 | EN 573-3, EN 485 | Strip, Sheet, Plate | ||
Elastic modulus | 72.0 GPa | T652 | EN 573-3, EN 485 | Strip, Sheet, Plate | ||
Elongation | 1.0 % | T652 | EN 573-3, EN 485 | Strip, Sheet, Plate | A100 | |
2.0 % | T652 | EN 573-3, EN 485 | Strip, Sheet, Plate | A100 | ||
4.0 % | T652 | EN 573-3, EN 485 | Strip, Sheet, Plate | A100 | ||
5.0 % | T652 | EN 573-3, EN 485 | Strip, Sheet, Plate | A100 | ||
6.0 % | T652 | EN 573-3, EN 485 | Strip, Sheet, Plate | A100 | ||
20.0 °C | 1.0 % | T652 | EN 573-3 | Flat | Transverse | |
20.0 °C | 1.0 % | T652 | EN 573-3 | Sheet | ||
20.0 °C | 2.0 % | T652 | EN 573-3 | Flat | Transverse | |
20.0 °C | 2.0 % | T652 | EN 573-3 | Sheet | ||
20.0 °C | 4.0 % | T652 | EN 573-3 | Flat | Transverse | |
20.0 °C | 4.0 % | T652 | EN 573-3 | Sheet | ||
20.0 °C | 5.0 % | T652 | EN 573-3 | Flat | Transverse | |
20.0 °C | 5.0 % | T652 | EN 573-3 | Sheet | ||
20.0 °C | 6.0 % | T652 | EN 573-3 | Flat | Transverse | |
20.0 °C | 6.0 % | T652 | EN 573-3 | Flat | ||
Hardness, Brinell | 20.0 °C | 175.0 - 190.0 [-] | T652 | EN 573-3 | Flat | |
20.0 °C | 175.0 - 185.0 [-] | T652 | EN 573-3 | Flat, Sheet | ||
20.0 °C | 175.0 - 180.0 [-] | T652 | EN 573-3 | Flat, Sheet | ||
20.0 °C | 175.0 [-] | T652 | EN 573-3 | Flat, Sheet | ||
20.0 °C | 180.0 - 190.0 [-] | T652 | EN 573-3 | Flat | ||
20.0 °C | 180.0 - 185.0 [-] | T652 | EN 573-3 | Flat, Sheet | ||
20.0 °C | 180.0 [-] | T652 | EN 573-3 | Flat, Sheet | ||
20.0 °C | 185.0 - 190.0 [-] | T652 | EN 573-3 | Flat | ||
20.0 °C | 185.0 [-] | T652 | EN 573-3 | Flat, Sheet | ||
20.0 °C | 190.0 [-] | T652 | EN 573-3 | Flat | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 7000 Series Aluminium | ||||
Shear modulus | 27.1 GPa | T652 | EN 573-3, EN 485 | Strip, Sheet, Plate | ||
Tensile strength | 470.0 MPa | T652 | EN 573-3, EN 485 | Strip, Sheet, Plate | ||
505.0 MPa | T652 | EN 573-3, EN 485 | Strip, Sheet, Plate | |||
525.0 MPa | T652 | EN 573-3, EN 485 | Strip, Sheet, Plate | |||
540.0 MPa | T652 | EN 573-3, EN 485 | Strip, Sheet, Plate | |||
550.0 MPa | T652 | EN 573-3, EN 485 | Strip, Sheet, Plate | |||
560.0 MPa | T652 | EN 573-3, EN 485 | Strip, Sheet, Plate | |||
570.0 MPa | T652 | EN 573-3, EN 485 | Strip, Sheet, Plate | |||
20.0 °C | 470.0 MPa | T652 | EN 573-3 | Flat | Transverse | |
20.0 °C | 470.0 MPa | T652 | EN 573-3 | Sheet | ||
20.0 °C | 505.0 MPa | T652 | EN 573-3 | Flat | Transverse | |
20.0 °C | 505.0 MPa | T652 | EN 573-3 | Sheet | ||
20.0 °C | 525.0 MPa | T652 | EN 573-3 | Flat | Transverse | |
20.0 °C | 525.0 MPa | T652 | EN 573-3 | Sheet | ||
20.0 °C | 540.0 MPa | T652 | EN 573-3 | Flat | Transverse | |
20.0 °C | 540.0 MPa | T652 | EN 573-3 | Sheet | ||
20.0 °C | 550.0 MPa | T652 | EN 573-3 | Flat | Transverse | |
20.0 °C | 550.0 MPa | T652 | EN 573-3 | Sheet | ||
20.0 °C | 560.0 MPa | T652 | EN 573-3 | Flat | Transverse | |
20.0 °C | 560.0 MPa | T652 | EN 573-3 | Sheet | ||
20.0 °C | 570.0 MPa | T652 | EN 573-3 | Flat | Transverse | |
20.0 °C | 570.0 MPa | T652 | EN 573-3 | Flat |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.1e-05 - 2.4e-05 1/K | Typical for Wrought 7000 Series Aluminium |
Melting point | 465.0 - 655.0 °C | Typical for Wrought 7000 Series Aluminium |
Specific heat capacity | 795.0 - 1050.0 J/(kg·K) | Typical for Wrought 7000 Series Aluminium |
Thermal conductivity | 121.0 - 170.0 W/(m·K) | Typical for Wrought 7000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 34000000.0 S/m | Typical for Wrought 7000 Series Aluminium |
Electrical resistivity | 2.9e-08 - 5.6e-08 Ω·m | Typical for Wrought 7000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.05 % | T652 | EN 573-3, EN 485 | Flat, Sheet, Strip, Plate |
Copper | 1.5 - 2.0 % | T652 | EN 573-3, EN 485 | Flat, Sheet, Strip, Plate |
Iron | 0.15 % | T652 | EN 573-3 | Flat, Sheet |
0.15 % | T652 | EN 573-3, EN 485 | Strip, Sheet, Plate | |
Magnesium | 2.1 - 2.6 % | T652 | EN 573-3, EN 485 | Flat, Sheet, Strip, Plate |
Manganese | 0.1 % | T652 | EN 573-3, EN 485 | Flat, Sheet, Strip, Plate |
Nickel | 0.05 % | T652 | EN 573-3, EN 485 | Flat, Sheet, Strip, Plate |
Silicon | 0.12 % | T652 | EN 573-3, EN 485 | Flat, Sheet, Strip, Plate |
Titanium | 0.06 % | T652 | EN 573-3, EN 485 | Flat, Sheet, Strip, Plate |
Zinc | 5.7 - 6.7 % | T652 | EN 573-3, EN 485 | Flat, Sheet, Strip, Plate |
Zirconium | 0.1 - 0.16 % | T652 | EN 573-3, EN 485 | Flat, Sheet, Strip, Plate |
Technological properties
| Property | ||
|---|---|---|
| Brazing | Excellent | |
Metal
- EN 573-3 Grade 3.1255 T652 – High-Strength Aluminum Alloy with Superior Machinability and Weldability
- AW-7010 T74 Aluminium Alloy – EN 573-3 Grade, High-Strength, Age-Hardenable
- EN 573-3 Grade AW-7010 T7451 Aluminum Zinc Alloy – Technical Specifications
- AW-7010 T76 Aluminum Alloy – EN 573-3 Grade for High-Performance Applications
- AW-7010 T73 Aluminium Alloy – EN 573-3 Grade Specification
- EN 573-3 Grade AW-7010 T7351 – High‑Strength Age‑Hardenable AlZn Alloy
- EN 573-3 Grade AW-7010 T7651: High-Performance Age-Hardenable AlZn Alloy
- AW-7010 T6: Premium EN 573-3 Grade Aluminum Alloy for Advanced Applications
- EN 573-3 Grade AW‑7010 T62: Premium Age‑Hardenable AlZn Alloy
- AW-7010 T651 (EN 573-3) – High-Strength Age-Hardenable AlZn Alloy