RM271 Epoxy Rods – High-Temperature Glass Fabric Composite with Superior Mechanical Performance
Rolled and Molded Rods made from a glass fabric with a high temperature epoxy resin system.
Properties
General
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Density | 1.8 g/cm³ | ASTM D349 | |
Moisture absorption | 0.06 % | ASTM D349 | Condition D₁-24/23 |
Mechanical
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Compressive modulus | 8.6 GPa | ASTM D349 | Condition A |
Compressive strength | 499.9 MPa | ASTM D349 | Condition A |
Flexural strength | 568.8 MPa | ASTM D349 | Condition A |
Hardness, Rockwell M | 110 [-] | ASTM D349 | |
Tensile strength | 344.7 MPa | ASTM D349 | Condition A |
Thermal
| Property | Value |
|---|---|
Flammability | UL 94, Class HB |
Technological properties
| Property | ||
|---|---|---|
| Application areas | RM271 is used in applications requiring low moisture absorption. | |
| Fillers | Glass Fabric | |
| Other | The mechanical properties are converted from American unit system to International unit system. | |
| Supplier Disclaimer | This data, while believed to be accurate and based on reliable analytical methods, is for informational purposes only. The terms and conditions of the agreement under which it is sold will govern any sales of this product. Data supplied above are "typical values"; not to be considered "specification values". To assure the material's performance is adequate for a specific application; customers should verify, independent of Norplex-Micarta, performance characteristics of interest. It is the responsibility of the users of this information to make sure that they have the latest version of this TDB, and are urged to check with Customer Service or, preferably our web site, www.norplex-micarta.com, to determine if the information is the most current available. | |
Composite material
- High-Performance Epoxy RM326 Rods – Durable, Strong, and Precision Molded
- RM310 Phenolic Rod – Superior Strength & Low Moisture Absorption
- Phenolic RM315 Rod – High-Strength, Low-Moisture Composite for Industrial Use
- RM320H Phenolic Rods – Heat‑Treated, High‑Strength Composite
- Epoxy RM500A Rods – Superior Electrical & Physical Performance
- RM629 Phenolic Resin Rod – High‑Performance Electrical & Mechanical Grade
- RM130 Epoxy Rods: High-Performance Flame Retardant Glass Fabric with Superior Electrical & Physical Properties
- RM504 Phenolic Rod – High-Performance Fiber‑Glass Composite for Mechanical & Low‑Voltage Electrical Applications
- Melamine RM505 Rods – High-Performance Thermal & Arc Resistant Composite Rods
- RM310E Phenolic Composite Rods – Superior Strength & Durability