Phenolic NP605 Sheet – Durable, Low-Resin Laminate for Hard, Flat Surfaces
A paper-base laminate with low phenolic resin content for hard, flat surfaces.
Properties
General
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Density | 1.3 g/cm³ | ASTM D792 | |
Moisture absorption | 8 % | ASTM D570 | Condition D₁-24/23 |
Mechanical
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Compressive strength | 241.3 MPa | ASTM D695 | Condition A | Flatwise |
Flexural strength | 172.4 MPa | ASTM D790 | Condition A |
172.4 MPa | ASTM D790 | Condition A, Transverse | |
Hardness, Rockwell M | 90 [-] | ASTM D785 | |
Impact strength, Izod unnotched, ASTM | 27 J/m | ASTM D256 | Condition E-48/50, Transverse |
29 J/m | ASTM D256 | Condition E-48/50 | |
Tensile strength | 117.2 MPa | ASTM D638 | Condition A |
Thermal
| Property | Value | Comment | |
|---|---|---|---|
Relative temperature index, mechanical strength | 150 °C | UL Bulletin 746b¹ | |
Flammability | UL Bulletin 94, Class HB, Condition A | ||
Technological properties
| Property | ||
|---|---|---|
| Application areas | This material is normally used in the printed circuit board industry as a backup for the drilling operation. However, it is also used in other industries for tooling stock because of its ease of machining and good dimensional stability. | |
| Fillers | Paper | |
| Other | 1.This temperature is a recommendation only, and based upon experience in various applications. The maximum operating temperature is dependent upon the application and should be investigated prior to use | |
| Supplier Disclaimer | This data, while believed to be accurate and based on reliable analytical methods, is for informational purposes only. The terms and conditions of the agreement under which it is sold will govern any sales of this product. Data supplied above are "typical values"; not to be considered "specification values". To assure the material's performance is adequate for a specific application; customers should verify, independent of Norplex-Micarta, performance characteristics of interest. It is the responsibility of the users of this information to make sure that they have the latest version of this TDB, and are urged to check with Customer Service or, preferably our web site, www.norplex-micarta.com, to determine if the information is the most current available. | |
Composite material
- BP11MPN Phenolic Composite Sheet – Superior Medium‑Weave Cotton Performance
- MC223 Medium-Weave Cotton Phenolic Sheet – High Performance Composite
- NP313HT Phenolic Sheet – Durable, Semi-Conductive, Low-Wear Performance
- Phenolic BP15NPN Sheet – Durable Post-Forming Canvas
- NP504 Phenolic Sheet – 175°C Rated, Superior Flexural & Impact Strength
- Phenolic NP310E Sheet: Superior Strength & Low Moisture for Precision Applications
- NP342 Phenolic Sheet – Military‑Grade Performance & Cost‑Effective Machining
- MC320LE Phenolic Composite Sheet – Superior Strength & Low Moisture Absorption
- NP318 Phenolic Sheet – High-Performance Post-Forming Canvas
- Phenolic NP615 Sheet – Flexible, High‑Resin, Arc‑Resistant Sheet Material