EN S355G10 Thermomechanically Rolled Steel (+M) – Superior Workability & Weldability
This steel is thermomechanically rolled (M) or normalised (N).
Our products are studied to improve workability and weldability.
Properties
General
| Property | Value | Comment | |
|---|---|---|---|
Carbon equivalent (CEV) | 0.41 [-] | Indicative value | Product | |
Weld cracking parameter | 0.21 [-] | Product | |
Carbon equivalent note | CEV = C + Mn/6 + (Cr+Mo+V)/5 + (Cu+Ni)/15 and PCM = C + Si/30 + (Cr+Mn+Cu)/20 + Ni/60 + Mo/15 + V/10 + 5B | ||
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Charpy impact energy | -40 °C | 50 J | min. | for thickness 5-40 mm | Transverse |
Elongation | 22 % | min. A5.65√So | for thickness 5-40 mm | Transverse | |
Tensile strength | 470 - 630 MPa | for thickness 5-40 mm | Transverse | |
Yield strength | 345 MPa | min. | for thickness 25-40 mm | Transverse | |
355 MPa | min. | for thickness 5-25 mm | Transverse | ||
Yield to strength ratio | 0.85 [-] | max | for thickness 16-25 mm | Transverse | |
0.87 [-] | max | for thickness 5-16 mm | Transverse |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Aluminium | 0.015 - 0.055 % | for thickness 5-40 mm |
Carbon | 0.12 % | max. | for thickness 5-40 mm |
Chromium | 0.2 % | max. | for thickness 5-40 mm |
Copper | 0.3 % | max. | for thickness 5-40 mm |
Manganese | 1.65 % | max. | for thickness 5-40 mm |
Molybdenum | 0.08 % | max. | for thickness 5-40 mm |
Nickel | 0.7 % | max. | for thickness 5-40 mm |
Niobium | 0.03 % | max. | for thickness 5-40 mm |
Nitrogen | 0.01 % | max. | for thickness 5-40 mm |
Phosphorus | 0.015 % | max. | for thickness 5-40 mm |
Silicon | 0.15 - 0.55 % | for thickness 5-40 mm |
Sulfur | 0.005 % | max. | for thickness 5-40 mm |
Titanium | 0.025 % | max. | for thickness 5-40 mm |
Vanadium | 0.06 % | max. | for thickness 5-40 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Offshore structures such as platforms and equipment for new offshore windmill towers. | |
| Chemical composition | The above chemical properties are based on cast analysis data. Product analysis may be requested at the time of order. | |
| Delivery condtion | For the dimensions available please visit Dimension tables (see Table A). Table A with a thickness range as indicated in the Mechanical properties. | |
| Other | Available options Options available (after previous agreement): | |
Metal
- EN 10225 S355G7 Thermomechanically Rolled (+M) Steel – High Workability & Weldability
- EN 10225 S355G8 Thermomechanically Rolled Steel (+M) – High Strength & Excellent Weldability
- EN AW-5083 Aluminum Rolled Plate – High Strength, Corrosion‑Resistant
- EN AW 6082 Aluminum Rolled Plate – High Strength, Excellent Stress Corrosion Resistance
- CERTAL® Aluminum Rolled Plate – High Strength & Dimensional Stability, EN AW 7022 (AlZn5Mg3Cu)
- EN AW-7075 Rolled Aluminum Plate – High Strength & Corrosion Resistance
- UNIDAL® Precision Al Zn4Mg2 Rolled Plate – High Flatness & Low Stress for Anodizing & Welding
- EN 10208-2 Grade L290MB Thermomechanically Rolled Steel – High-Strength, Weldable Pipe for Flammable Media
- EN 10208-2 L360MB Thermomechanically Rolled Steel Pipe – High Yield, Weldable for Flammable Liquids
- EN 10208-2 Grade L245MB Thermomechanically Rolled Steel Pipe for Flammable Media