JIS H4001 Grade 3005 Aluminium – ¾ Hard Annealed (Mechanical & Physical Properties)
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.72 - 2.73 g/cm³ | Typical for Wrought 3000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 69.5 - 70.0 GPa | Typical for Wrought 3000 Series Aluminium | ||
Elongation | 2.0 % | annealed at 3/4 hard | JIS H4001 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||
Shear modulus | 25.0 - 26.0 GPa | Typical for Wrought 3000 Series Aluminium | ||
Tensile strength | 196.0 MPa | annealed at 3/4 hard | JIS H4001 | |
Yield strength | 167.0 MPa | annealed at 3/4 hard | JIS H4001 |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.4e-05 1/K | Typical for Wrought 3000 Series Aluminium |
Melting point | 629.0 - 654.0 °C | Typical for Wrought 3000 Series Aluminium |
Specific heat capacity | 893.0 - 920.0 J/(kg·K) | Typical for Wrought 3000 Series Aluminium |
Thermal conductivity | 154.0 - 193.0 W/(m·K) | Typical for Wrought 3000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 23000000.0 - 29000000.0 S/m | Typical for Wrought 3000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 4.2e-08 Ω·m | Typical for Wrought 3000 Series Aluminium |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |
Metal
- JIS H4001 Grade 3004 Aluminium – ½ Hard Condition for Optimal Performance
- JIS H4001 Grade 3004 Aluminum: ¼‑Hard Stabilized for Superior Performance
- JIS H4001 Grade 3004 Aluminium – 3/4 Hard Stabilized, Optimal Strength & Durability
- JIS H4001 Grade 3005 H24 – High-Strength 3000 Series Aluminium Alloy
- JIS H4001 Grade 3005H22 Aluminium Sheet – High Strength, Excellent Toughness
- JIS H4000 Grade 5083 Aluminium – 1/4 Hard Stabilized, Mechanical Properties & Standards
- JIS H4120 Grade 2017: 3/8 Hard Aluminum Alloy for Superior Strength and Machinability
- JIS G3141 Grade SPCC 1/4 Hard Steel – Key Properties & Specifications
- JIS G3141 Grade SPCD 1/4 Hard – Key Properties & Specs
- JIS G3141 Grade SPCE 1/4 Hard Steel – Specifications & Mechanical Properties