ASTM A803 Grade 29-4-2 – Solution-Annealed Stainless Steel: Properties & Specs

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	7.6 - 7.8 g/cm³	Typical for Ferritic Stainless Steel

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	220 GPa	Typical for Ferritic Stainless Steel
Elongation A50	23.0 °C	20 %
Hardness, Brinell	23.0 °C	241 [-]
Hardness, Rockwell B	23.0 °C	100 [-]
Poisson's ratio	23.0 °C	0.3 [-]	Typical for Ferritic Stainless Steel
Shear modulus	23.0 °C	77 GPa	Typical for Ferritic Stainless Steel
Tensile strength	23.0 °C	550 MPa
Yield strength	23.0 °C	415 MPa

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	9.3E-6 - 1.2E-5 1/K	Typical for Ferritic Stainless Steel
Melting point		1425 - 1530 °C	Typical for Ferritic Stainless Steel
Specific heat capacity	23.0 °C	420 - 586 J/(kg·K)	Typical for Ferritic Stainless Steel
Thermal conductivity	23.0 °C	11 - 22 W/(m·K)	Typical for Ferritic Stainless Steel

Electrical

Property	Temperature	Value	Comment
Electrical resistivity	23.0 °C	6E-7 - 7.5E-7 Ω·m	Typical for Ferritic Stainless Steel

Chemical properties

Property	Value
Carbon	0.01 %
Chromium	28 - 30 %
Copper	0.15 %
Manganese	0.3 %
Molybdenum	3.5 - 4.2 %
Nickel	2 - 2.5 %
Nitrogen	0.02 %
Phosphorus	0.03 %
Silicon	0.2 %
Sulfur	0.02 %

ASTM A803 Grade 26-3-3 Solution-Annealed Stainless Steel – Premium Ferritic Performance ASTM A803 TP439 Solution-Annealed Stainless Steel – Detailed Properties & Performance