ASTM A182 Grade F429 Annealed Stainless Steel – Properties & Applications

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	7.6 - 7.8 g/cm³	Typical for Ferritic Stainless Steel

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	220 GPa	Typical for Ferritic Stainless Steel
Elongation A50	23.0 °C	20 %
Hardness, Brinell	23.0 °C	190 [-]
Poisson's ratio	23.0 °C	0.3 [-]	Typical for Ferritic Stainless Steel
Reduction of area	23.0 °C	45 %
Shear modulus	23.0 °C	77 GPa	Typical for Ferritic Stainless Steel
Tensile strength	23.0 °C	415 MPa
Yield strength Rp0.2	23.0 °C	240 MPa

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	9.3E-6 - 1.2E-5 1/K	Typical for Ferritic Stainless Steel
Melting point		1425 - 1530 °C	Typical for Ferritic Stainless Steel
Specific heat capacity	23.0 °C	420 - 586 J/(kg·K)	Typical for Ferritic Stainless Steel
Thermal conductivity	23.0 °C	11 - 22 W/(m·K)	Typical for Ferritic Stainless Steel

Electrical

Property	Temperature	Value	Comment
Electrical resistivity	23.0 °C	6E-7 - 7.5E-7 Ω·m	Typical for Ferritic Stainless Steel

Chemical properties

Property	Value
Carbon	0.12 %
Chromium	14 - 16 %
Manganese	1 %
Nickel	0.5 %
Phosphorus	0.04 %
Silicon	0.75 %
Sulfur	0.03 %