EN 1652 CuZn37Pb0.5 H110: High-Performance Unhardenable Brass Alloy

CuNi10Fe1Mn (CW352H) is comparable to CuNi10Fe1Mn, mat. no. 2.0872, acc. to DIN 17664 : 1983-12. To the comparable DIN-mark applies: The material shows favorable specific strength values also at endurance loading and increased temperatures. Thermal conductivity of pure copper is strongly reduced by

CuNi2Si, mat. No CW111C, is counted among hardenable, low alloyed copper alloys. To the comparable make CuBNi2Si, mat. No 2.0855, acc. to DIN 17666 : 1983-12 applies: The material shows favorable electrical and thermal conductivity, corrosion resistance, high fatigue and creep resistance as well as

CuBe2, mat. No CW101C, is counted among hardenable, low alloyed copper alloys. To the comparable make CuBe2, mat. No 2.1247, acc. to DIN 17666 : 1983-12 applies: It is an alloy of optimal hardenability for highest requirements to strength, elasticity, abrasion and fatigue resistance. CuBe2 shows mea

Cuco2Be, mat. No CW104C, is counted among hardenable, low alloyed copper alloys. To the comparable make Cuco2Be, mat. No 2.1285, acc. to DIN 17666 : 1983-12 applies: CuCo2Be achieves compared to CuBe2 at slightly lower hardness and strength values higher electrical and thermal conductivity. The temp