EN 12166 CuNi12Zn24 R800 – High‑Strength, Corrosion‑Resistant Copper Alloy
Material CuNi12Zn24, mat. No. CW403J is an alloy of high strength and hardness. To the comparabel DIN-mark CuNi12Zn24, mat. No. 2.0730, acc. to DIN 17663 : 1983-12 applies: Strength is further increasable due to the high strain hardening capability. The material does not embrittle at low temperatures. Low electrical and thermal conductivity. The alloy is non-magnetic, corrosion resistance is better than for pure copper. Processing properties: warm forming: moderately cold forming: very good machinability: moderately hard and soft soldering: very good TIG-welding: very good burnishing: very good Application: In electrical engineering and electronics for springs, contacts, membranes as well as in precision engineering and in equipment manufacturing. In food industry, for musical instruments, glasses frames, safety keys as well as in construction trade for paneling, show-cases and stairrails.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.67 - 8.7 g/cm³ |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 20.0 °C | 125 GPa |
Poisson's ratio | 20.0 °C | 0.34 [-] |
Tensile strength | 20.0 °C | 800 MPa |
Yield strength Rp0.2 | 20.0 °C | 700 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 300.0 °C | 1.65E-5 1/K | |
Melting point | 875 - 1135 °C | Typical for Wrought Copper Nickel Silver Grade | |
Specific heat capacity | 20.0 °C | 380 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 42 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 4.40E+6 S/m |
Specific Electrical conductivity | 8 % IACS |
Chemical properties
| Property | Value |
|---|---|
Copper | 63 - 66 % |
Iron | 0.3 % |
Lead | 0.03 % |
Manganese | 0.5 % |
Nickel | 11 - 13 % |
Tin | 0.03 % |
Metal
- EN 12166 Grade CuNi18Zn20 H01 – High Strength, Corrosion-Resistant Copper–Nickel–Zinc Alloy
- EN 12166 Copper Brass Grade CuZn15 R310 – Specifications & Properties
- EN 12166 CuZn30 H00 Wrought Copper Alloy – Superior Strength and Corrosion Resistance
- EN 12166 Grade CuZn36 R360 – Premium Beryllium Copper Alloy
- EN 12166 Grade CuNi10Zn27 H01: High-Performance Copper-Nickel-Zinc Alloy Wire
- EN 12166 CuNi12Zn24 H01 – High Strength, Corrosion-Resistant Copper-Nickel-Zinc Alloy
- EN 12166 Grade CuNi18Zn20 R800: Premium High-Strength Copper‑Nickel‑Zinc Alloy
- EN 12166: Grade CuZr M – Premium Low‑Alloy Copper with Superior Strength and Conductivity
- EN 12166 Grade CuBe2 TD – Premium Hardenable Copper-Beryllium Alloy
- EN 12166 Grade CuNi12Zn24 O60 – High-Strength, Corrosion-Resistant Copper-Nickel-Zinc Alloy