EN 12167 CuCo₂Be H230: High-Performance Copper Alloy
Cuco2Be, mat. No CW104C, is counted among hardenable, low alloyed copper alloys. To the comparable make Cuco2Be, mat. No 2.1285, acc. to DIN 17666 : 1983-12 applies: CuCo2Be achieves compared to CuBe2 at slightly lower hardness and strength values higher electrical and thermal conductivity. The temperature for removal of workhardening approximates 500°C, high corrosion resistance. Processing properties: hot and cold forming: good machinability: moderately hard and soft soldering: good gas shielded welding: good burnishing: good Application: In relay and switch construction for high loadable, live springs and for radiant heaters at semi conductors. Furthermore for resistance and welding electrodes as well as for pistons, plunger and punching tools. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.8 - 8.9 g/cm³ |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 20.0 °C | 138 GPa |
Hardness, Brinell | 20.0 °C | 230 - 310 [-] |
Hardness, Vickers | 20.0 °C | 230 - 290 [-] |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 300.0 °C | 1.8E-5 1/K | |
Max service temperature, long | 0 - 350 °C | ||
Melting point | 855 - 1090 °C | Typical for Wrought Copper High Copper Alloy | |
Specific heat capacity | 23.0 °C | 360 - 420 J/(kg·K) | Typical for Wrought Copper High Copper Alloy |
Thermal conductivity | 20.0 °C | 192 - 239 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 2.50E+7 - 3.20E+7 S/m |
Specific Electrical conductivity | 43 % IACS |
Chemical properties
| Property | Value |
|---|---|
Beryllium | 0.4 - 0.7 % |
Cobalt | 2 - 2.8 % |
Iron | 0.2 % |
Nickel | 0.3 % |
Metal
- EN 12163 Grade CuCo2Be F00: High-Performance Low-Alloy Copper Alloy
- EN 12163 Grade CuCo2Be TB00 – Premium Low‑Alloy Copper Alloy
- EN 12167 Grade CuZn43Pb2 R430 – Leaded Brass Alloy with Enhanced Machinability
- EN 12167 Grade CuZn43Pb2 R480 – Lead-Containing Brass Alloy
- EN 12167 Grade CuZn38Pb1 H105 – High-Quality Copper Alloy Tubes
- EN 12166 Grade CuCo2Be H230 – Premium High‑Copper Alloy Wire for Springs and Fasteners
- EN 12163 Grade CuCo2Be H230 – High-Performance Low‑Alloy Copper Alloy
- EN 12167 CuCo2Be R730 – High‑Performance Low‑Carbon Copper Alloy
- EN 12167 CuCo₂Be R680: High-Conductivity, Corrosion-Resistant Low-Alloy Copper
- EN 1652 Grade CuCo2Be TH: High-Performance Low-Alloy Copper Alloy with Superior Conductivity