EN 12167 CuZn37Mn3Al2PbSi Copper Alloy – High Strength & Corrosion Resistance
CuZn37Mn3Al2PbSi (CW713R former CuZn40Al2) is an unhardenable copper alloy. High hardness and strength parameter are achievable by cold forming only. Strength properties, corrosion resistance and oxidation resistance are increasable by Al-addition. CuZn37Mn3Al2PbSi shows a high wear resistance and is favorable resistant to atmospheric corrosion, to low aggressive water and gas, insensitive to oil corrosion. Processing properties: warm forming: very good cold forming: unfavorable machinability: moderately hard soldering: moderately soft soldering: unfavorable TIG-welding: moderately burnishing: very good Application for construction parts in machine engineering, for friction bearings, valve guides, transmission parts and piston rings.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.1 - 8.12 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 93 GPa | |
Hardness, Brinell | 20.0 °C | 160 [-] | |
Hardness, Vickers | 20.0 °C | 170 [-] | |
Shear modulus | 23.0 °C | 40 GPa | Typical for Wrought Copper Brass |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.95E-5 1/K | |
300.0 °C | 2.04E-5 1/K | ||
Melting point | 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 20.0 °C | 377 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 63 W/(m·K) | |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 7.80E+6 S/m |
Specific Electrical conductivity | 13.4 % IACS |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 1.3 - 2.3 % |
Copper | 56.5 - 59 % |
Iron | 1 % |
Lead | 0.8 % |
Manganese | 1.4 - 2.6 % |
Nickel | 2 % |
Silicon | 0.3 - 1 % |
Tin | 0.5 % |
Metal
- EN 12167 Grade CuZn43Pb2 R430 – Leaded Brass Alloy with Enhanced Machinability
- EN 12167 Grade CuZn43Pb2 R480 – Lead-Containing Brass Alloy
- EN 12167 Grade CuZn38Pb1 H105 – High-Quality Copper Alloy Tubes
- EN 12167 Grade R490: CuZn39Mn1AlPbSi Copper Alloy – Superior Strength & Corrosion Resistance
- EN 12167 Grade CuZn40Mn1Pb1AlFeSn H110 – Premium Brass Rods & Forged Components
- EN 12167 Grade CuZn40Mn1Pb1AlFeSn R490 – Premium Brass Alloy for Industrial Applications
- EN 12167 Grade R420 CuZn40Mn2Fe1 – High-Strength, Corrosion-Resistant Copper Alloy
- EN 12167 CuZn40Mn2Fe1 – Weather‑Resistant, High‑Strength Copper Alloy for Cold Forming
- EN 12167 CuZn43Pb2 H110 Brass Alloy – Properties & Applications
- EN 12167 CuAl10Fe3Mn2 H160: High-Strength, Cold-Formable Wrought Alloy