EN 12167 Grade CuZn40Mn1Pb1AlFeSn H110 – Premium Brass Rods & Forged Components
Material CuZn40Mn1Pb1AlFeSn (CW721R) is used in the form of rods, hollow rods, profiles, forging prematerial and forged parts.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.3 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 96 GPa | |
Hardness, Brinell | 20.0 °C | 110 [-] | |
Hardness, Vickers | 20.0 °C | 115 [-] | |
Shear modulus | 23.0 °C | 40 GPa | Typical for Wrought Copper Brass |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.7E-5 - 2.1E-5 1/K | Typical for Wrought Copper Brass |
Melting point | 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 20.0 °C | 377 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 88 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 9.00E+6 S/m |
Specific Electrical conductivity | 15.5 % IACS |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 0.3 - 1.3 % |
Copper | 57 - 59 % |
Iron | 0.2 - 1.2 % |
Lead | 0.8 - 1.6 % |
Manganese | 0.8 - 1.8 % |
Nickel | 0.3 % |
Tin | 0.2 - 1 % |
Metal
- EN 1652 Grade CuZn38Pb2 H110 – Premium Wrought Copper Brass
- EN 1652 CuZn0.5 H110 Copper Alloy – High-Quality Plate, Sheet, and Strip
- EN 1652 CuZn37Pb0.5 H110: High-Performance Unhardenable Brass Alloy
- EN 1652 CuZn5 H110 – Premium Copper Alloy for Electrical & Shock-Absorbing Applications
- EN 12167 Grade CuZn40Mn1Pb1AlFeSn R490 – Premium Brass Alloy for Industrial Applications
- EN 12167 CuZn43Pb2 H110 Brass Alloy – Properties & Applications
- EN 12167 Grade CuZn35Ni3Mn2AlPb H110 – High-Strength Unhardenable Copper Alloy
- EN 12167 Grade CuZn37 H110 – High-Strength, Corrosion-Resistant Copper Alloy
- EN 12167 CuZn39Mn1AlPbSi (CW718R) – Unhardenable Copper Alloy with Enhanced Strength & Corrosion Resistance
- EN 12167 Grade CuZn39Pb3 H110 – Premium Leaded Brass Alloy for Superior Machinability