EN 12167 CuZn39Mn1AlPbSi (CW718R) – Unhardenable Copper Alloy with Enhanced Strength & Corrosion Resistance
CuZn39Mn1AlPbSi (CW718R former identification: CuZn40Al1) is an unhardenable copper alloy. High hardness and strength values are achievable by cold forming only. Strength properties, corrosion resistance and oxidation resistance are increasable by Al-addition. CuZn39Mn1AlPbSi shows a mean wear resistance and favorable siding qualities. Processing properties: warm forming: very good cold forming: unfavorable machinability: moderately hard soldering: moderately soft soldering: unfavorable TIG-welding: moderately burnishing: very good The material is applicated for steering knuckle bushings, sliding bearings, sliding elements, worm gear rims and pinion gears.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.2 g/cm³ |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 20.0 °C | 106 GPa |
Elongation | 20.0 °C | 15 % |
Hardness, Brinell | 20.0 °C | 110 [-] |
Hardness, Vickers | 20.0 °C | 115 [-] |
Shear modulus | 20.0 °C | 40 GPa |
Tensile strength | 20.0 °C | 440 MPa |
Yield strength Rp0.2 | 20.0 °C | 180 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 95.0 °C | 2.16E-5 1/K | |
Melting point | 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 23.0 °C | 371 - 418 J/(kg·K) | Typical for Wrought Copper Brass |
Thermal conductivity | 20.0 °C | 71 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 9.10E+6 S/m |
Electrical resistivity | 20.0 °C | 1.1E-7 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 0.4 - 1.3 % |
Copper | 57.5 - 60 % |
Iron | 1 % |
Lead | 0.8 % |
Manganese | 0.8 - 1.8 % |
Nickel | 1 % |
Silicon | 0.7 % |
Tin | 0.4 % |
Metal
- EN 1652 Grade CuZn38Pb2 H110 – Premium Wrought Copper Brass
- EN 1652 CuZn0.5 H110 Copper Alloy – High-Quality Plate, Sheet, and Strip
- EN 1652 CuZn37Pb0.5 H110: High-Performance Unhardenable Brass Alloy
- EN 1652 CuZn5 H110 – Premium Copper Alloy for Electrical & Shock-Absorbing Applications
- EN 12167 Grade R490: CuZn39Mn1AlPbSi Copper Alloy – Superior Strength & Corrosion Resistance
- EN 12167 Grade CuZn40Mn1Pb1AlFeSn H110 – Premium Brass Rods & Forged Components
- EN 12167 CuZn43Pb2 H110 Brass Alloy – Properties & Applications
- EN 12167 Grade CuZn35Ni3Mn2AlPb H110 – High-Strength Unhardenable Copper Alloy
- EN 12167 Grade CuZn37 H110 – High-Strength, Corrosion-Resistant Copper Alloy
- EN 12167 Grade CuZn39Pb3 H110 – Premium Leaded Brass Alloy for Superior Machinability