EN 12167 Grade CuZn39Pb3 H110 – Premium Leaded Brass Alloy for Superior Machinability

Material CuZn39Pb3, mat. No. CW614N, is an unhardenable wrought alloy. to the comparable make CuZn39Pb3, mat. No. 2.0401 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for unleaded brass of the same Zn-content. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: very good cold forming: unfavorable machinability: very good hard soldering: moderately soft soldering: very good TIG-welding: unfavorable burnishing: very good Application: Main alloy of the brass materials for machining on automats. Use for all types of form turning parts, in precision engineering as well as in watch and electrical industry.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.4 - 8.47 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

96 - 97 GPa

Hardness, Brinell

20.0 °C

110 - 160 [-]

Hardness, Vickers

20.0 °C

120 - 170 [-]

Shear modulus

23.0 °C

40 GPa

Typical for Wrought Copper Brass

Tensile strength

20.0 °C

430 MPa

Yield strength Rp0.2

20.0 °C

250 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

100.0 °C

1.93E-5 1/K

200.0 °C

2.1E-5 1/K

300.0 °C

2.14E-5 1/K

800.0 °C

2.47E-5 1/K

Melting point

875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 J/(kg·K)

Thermal conductivity

-200.0 °C

50 W/(m·K)

20.0 °C

113 - 123 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.46E+7 - 1.50E+7 S/m

200.0 °C

1.20E+7 S/m

Electrical resistivity

20.0 °C

6.6E-8 Ω·m

200.0 °C

8.3E-8 Ω·m

Specific Electrical conductivity

25 - 25.2 % IACS

Chemical properties

PropertyValue

Aluminium

0.05 %

Copper

57 - 59 %

Iron

0.3 %

Lead

2.5 - 3.5 %

Nickel

0.3 %

Tin

0.3 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 1652 Grade CuZn38Pb2 H110 – Premium Wrought Copper Brass
    2. EN 1652 CuZn0.5 H110 Copper Alloy – High-Quality Plate, Sheet, and Strip
    3. EN 12167 Grade CuZn40Mn1Pb1AlFeSn H110 – Premium Brass Rods & Forged Components
    4. EN 12167 CuZn43Pb2 H110 Brass Alloy – Properties & Applications
    5. EN 12167 Grade CuZn35Ni3Mn2AlPb H110 – High-Strength Unhardenable Copper Alloy
    6. EN 12167 Grade CuZn37 H110 – High-Strength, Corrosion-Resistant Copper Alloy
    7. EN 12167 CuZn39Mn1AlPbSi (CW718R) – Unhardenable Copper Alloy with Enhanced Strength & Corrosion Resistance
    8. EN 12167 Grade CuZn39Pb3 H090 – Unhardenable Wrought Brass Alloy
    9. EN 12166 Grade CuZn39Pb3 H110 – High-Strength, Lead-Enhanced Brass Alloy
    10. EN 12167 Grade O60 CuZn39Pb3 Leaded Brass Alloy – High Hardness & Machinability