EN 12167 Grade CuZn39Pb3 H090 – Unhardenable Wrought Brass Alloy
Material CuZn39Pb3, mat. No. CW614N, is an unhardenable wrought alloy. to the comparable make CuZn39Pb3, mat. No. 2.0401 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for unleaded brass of the same Zn-content. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: very good cold forming: unfavorable machinability: very good hard soldering: moderately soft soldering: very good TIG-welding: unfavorable burnishing: very good Application: Main alloy of the brass materials for machining on automats. Use for all types of form turning parts, in precision engineering as well as in watch and electrical industry.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.4 - 8.47 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 96 - 97 GPa | |
Hardness, Brinell | 20.0 °C | 90 - 140 [-] | |
Hardness, Vickers | 20.0 °C | 100 - 150 [-] | |
Shear modulus | 23.0 °C | 40 GPa | Typical for Wrought Copper Brass |
Tensile strength | 20.0 °C | 380 MPa | |
Yield strength Rp0.2 | 20.0 °C | 160 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.93E-5 1/K | |
200.0 °C | 2.1E-5 1/K | ||
300.0 °C | 2.14E-5 1/K | ||
800.0 °C | 2.47E-5 1/K | ||
Melting point | 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 20.0 °C | 377 J/(kg·K) | |
Thermal conductivity | -200.0 °C | 50 W/(m·K) | |
20.0 °C | 113 - 123 W/(m·K) | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 1.46E+7 - 1.50E+7 S/m |
200.0 °C | 1.20E+7 S/m | |
Electrical resistivity | 20.0 °C | 6.6E-8 Ω·m |
200.0 °C | 8.3E-8 Ω·m | |
Specific Electrical conductivity | 25 - 25.2 % IACS | |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 0.05 % |
Copper | 57 - 59 % |
Iron | 0.3 % |
Lead | 2.5 - 3.5 % |
Nickel | 0.3 % |
Tin | 0.3 % |
Metal
- EN 12167 Grade CuZn43Pb2 R430 – Leaded Brass Alloy with Enhanced Machinability
- EN 12167 Grade CuZn43Pb2 R480 – Lead-Containing Brass Alloy
- EN 12167 Grade CuZr H090 – High-Performance Low-Alloy Copper Alloy
- EN 12167 Grade CuZn38Pb1 H105 – High-Quality Copper Alloy Tubes
- EN 12167 Grade R490: CuZn39Mn1AlPbSi Copper Alloy – Superior Strength & Corrosion Resistance
- EN 12167 CuZn36 – Unhardenable Copper Alloy for Precision Fabrication
- EN 12167 Grade CuZn37 H090 – Premium Cold‑Formed Copper Alloy for Industrial Applications
- EN 12167 Grade CuZn39Pb3 H110 – Premium Leaded Brass Alloy for Superior Machinability
- EN 12166 Grade CuZn39Pb3 H090 – Lead-Containing Brass Alloy
- EN 12167 Grade O60 CuZn39Pb3 Leaded Brass Alloy – High Hardness & Machinability