EN 12167 Grade O60 CuZn39Pb3 Leaded Brass Alloy – High Hardness & Machinability

Material CuZn39Pb3, mat. No. CW614N, is an unhardenable wrought alloy. to the comparable make CuZn39Pb3, mat. No. 2.0401 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for unleaded brass of the same Zn-content. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: very good cold forming: unfavorable machinability: very good hard soldering: moderately soft soldering: very good TIG-welding: unfavorable burnishing: very good Application: Main alloy of the brass materials for machining on automats. Use for all types of form turning parts, in precision engineering as well as in watch and electrical industry.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.4 - 8.47 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

96 - 97 GPa

Elongation

-196.0 °C

40 %

-78.0 °C

34 %

20.0 °C

25 - 33 %

Hardness, Brinell

20.0 °C

80 - 115 [-]

Hardness, Vickers

20.0 °C

85 - 120 [-]

Shear modulus

23.0 °C

40 GPa

Typical for Wrought Copper Brass

Tensile strength

-196.0 °C

575 MPa

-78.0 °C

460 MPa

20.0 °C

360 - 425 MPa

Yield strength Rp0.2

20.0 °C

250 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

100.0 °C

1.93E-5 1/K

200.0 °C

2.1E-5 1/K

300.0 °C

2.14E-5 1/K

800.0 °C

2.47E-5 1/K

Melting point

875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 J/(kg·K)

Thermal conductivity

-200.0 °C

50 W/(m·K)

20.0 °C

113 - 123 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.46E+7 - 1.50E+7 S/m

200.0 °C

1.20E+7 S/m

Electrical resistivity

20.0 °C

6.6E-8 Ω·m

200.0 °C

8.3E-8 Ω·m

Specific Electrical conductivity

25 - 25.2 % IACS

Chemical properties

PropertyValue

Aluminium

0.05 %

Copper

57 - 59 %

Iron

0.3 %

Lead

2.5 - 3.5 %

Nickel

0.3 %

Tin

0.3 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 12166 Grade CuNi10Zn27 O60: High-Performance Copper-Nickel-Zinc Wire
    2. EN 12167 Grade CuZn43Pb2 R430 – Leaded Brass Alloy with Enhanced Machinability
    3. EN 12167 Grade CuZn43Pb2 R480 – Lead-Containing Brass Alloy
    4. EN 12167 Grade CuZn38Pb1 H105 – High-Quality Copper Alloy Tubes
    5. EN 12167 Grade R490: CuZn39Mn1AlPbSi Copper Alloy – Superior Strength & Corrosion Resistance
    6. EN 12167 Grade CuZn40Mn1Pb1AlFeSn H110 – Premium Brass Rods & Forged Components
    7. EN 12167 Grade CuZn40Mn1Pb1AlFeSn R490 – Premium Brass Alloy for Industrial Applications
    8. EN 12167 Grade CuZn39Pb3 H110 – Premium Leaded Brass Alloy for Superior Machinability
    9. EN 12167 Grade CuZn39Pb3 H090 – Unhardenable Wrought Brass Alloy
    10. EN 12166 Grade CuZn39Pb3 – Leaded Brass with Enhanced Machinability