EN 12167 Grade CuZn37 H110 – High-Strength, Corrosion-Resistant Copper Alloy

CuZn37 (CW508L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn36. CuZn37 is the main alloy for cold forming. It shows favorable corrosion resistance to fresh water. Processing properties: warm forming: good cold forming: very good machinability: moderately hard soldering: good soft soldering: very good TIG-welding: moderately burnishing: very good CuZn37 is used for bulb bases, wire clamps for aerial lines, contact springs, metal and wooden screws, print roller and zip fastener. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.44 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

110 GPa

100.0 °C

106 GPa

200.0 °C

102 GPa

300.0 °C

97 GPa

400.0 °C

89 GPa

500.0 °C

79 GPa

Hardness, Brinell

20.0 °C

110 [-]

Hardness, Vickers

20.0 °C

115 [-]

Shear modulus

23.0 °C

40 GPa

Typical for Wrought Copper Brass

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

150.0 °C

1.9E-5 1/K

300.0 °C

2.1E-5 1/K

650.0 °C

2.3E-5 1/K

800.0 °C

2.4E-5 1/K

Melting point

875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 J/(kg·K)

Thermal conductivity

-200.0 °C

50 W/(m·K)

20.0 °C

120 W/(m·K)

200.0 °C

142 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.50E+7 S/m

200.0 °C

1.20E+7 S/m

Electrical resistivity

20.0 °C

6.6E-8 Ω·m

200.0 °C

8.3E-8 Ω·m

Chemical properties

PropertyValue

Aluminium

0.05 %

Copper

62 - 64 %

Iron

0.1 %

Lead

0.1 %

Nickel

0.3 %

Tin

0.1 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 1652 Grade CuZn38Pb2 H110 – Premium Wrought Copper Brass
    2. EN 1652 CuZn0.5 H110 Copper Alloy – High-Quality Plate, Sheet, and Strip
    3. EN 12167 Grade CuZn40Mn1Pb1AlFeSn H110 – Premium Brass Rods & Forged Components
    4. EN 12167 CuZn43Pb2 H110 Brass Alloy – Properties & Applications
    5. EN 12167 Grade CuZn35Ni3Mn2AlPb H110 – High-Strength Unhardenable Copper Alloy
    6. EN 12167 CuZn37 R400 – Premium Cold‑Formed Copper Alloy
    7. EN 12167 Grade CuZn37 H110 – High-Strength, Corrosion-Resistant Copper Alloy
    8. EN 12167 Grade CuZn37 H090 – Premium Cold‑Formed Copper Alloy for Industrial Applications
    9. EN 12167 CuZn39Mn1AlPbSi (CW718R) – Unhardenable Copper Alloy with Enhanced Strength & Corrosion Resistance
    10. EN 12167 Grade CuZn39Pb3 H110 – Premium Leaded Brass Alloy for Superior Machinability