EN 10028-7 Grade X2CrTi17 – Solution-Annealed Ferritic Stainless Steel for Automotive, Electrical, and Household Use

The ferritic stainless steel X2CrTi17 has a extremely low C-content for special applications in household, car and electrical industry.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.7 - 7.73 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

20.0 °C

217 - 220 GPa

100.0 °C

215 GPa

200.0 °C

188 - 210 GPa

300.0 °C

164 - 205 GPa

400.0 °C

195 GPa

Poisson's ratio

20.0 °C

0.29 [-]

Shear modulus

20.0 °C

84.82 GPa

Yield strength Rp0.2

50.0 °C

198 MPa

100.0 °C

195 MPa

150.0 °C

180 MPa

200.0 °C

170 MPa

250.0 °C

160 MPa

300.0 °C

155 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

20.0 °C

1.02E-5 1/K

100.0 °C

1.04E-5 - 1.05E-5 1/K

200.0 °C

1.08E-5 - 1.09E-5 1/K

300.0 °C

1.12E-5 - 1.13E-5 1/K

400.0 °C

1.16E-5 1/K

500.0 °C

1.19E-5 - 1.2E-5 1/K

600.0 °C

1.22E-5 1/K

Melting point

1425 - 1530 °C

Typical for Ferritic Stainless Steel

Specific heat capacity

20.0 °C

430 - 439 J/(kg·K)

100.0 °C

474 J/(kg·K)

200.0 °C

498 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

538 J/(kg·K)

500.0 °C

564 J/(kg·K)

600.0 °C

598 J/(kg·K)

Thermal conductivity

20.0 °C

20 - 25.9 W/(m·K)

100.0 °C

25.3 W/(m·K)

200.0 °C

25.2 W/(m·K)

300.0 °C

25.2 W/(m·K)

400.0 °C

25.4 W/(m·K)

500.0 °C

25.7 W/(m·K)

600.0 °C

25.9 W/(m·K)

Thermal diffusivity

20.0 °C

7.6 mm²/s

100.0 °C

6.6 mm²/s

200.0 °C

6.1 mm²/s

300.0 °C

5.8 mm²/s

400.0 °C

5.3 mm²/s

500.0 °C

4.8 mm²/s

600.0 °C

4.1 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

5.59E-7 - 7E-7 Ω·m

100.0 °C

6.4E-7 Ω·m

200.0 °C

7.32E-7 Ω·m

300.0 °C

8.17E-7 Ω·m

400.0 °C

8.97E-7 Ω·m

500.0 °C

9.74E-7 Ω·m

600.0 °C

1.05E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.025 %

Chromium

16 - 18 %

Manganese

0.5 %

Nitrogen

0.02 %

Phosphorus

0.04 %

Silicon

0.5 %

Sulfur

0.015 %

Titanium

0.3 - 0.6 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. X3CrTi17 Ferritic Steel – EN 10028-7 Grade, Solution Annealed (+AT) – Superior Corrosion Resistance
    2. EN 10028-7 Grade X2CrMoTi18-2: Solution-Annealed Ferritic Steel (+AT) – Superior Corrosion Resistance & Cold Forming
    3. EN 10028-7 Grade X2CrNi12: Solution-Annealed Steel with Superior Corrosion Resistance
    4. EN 10028-7 Grade X6CrNi23-13 Solution Annealed Steel – High-Temperature Resistant Alloy
    5. EN 10028-7 Grade X6CrNi25-20: Solution-Annealed Austenitic Steel for High-Temperature Applications
    6. EN 10028-7 X1CrNiMoCuN20-18-7 Solution‑Annealed Steel (AT) – Premium Corrosion Resistance
    7. EN 10028-7 Grade X1CrNiMoCuN25-25-5: High-Performance Austenitic Steel Solution-Annealed for Corrosion Resistance
    8. EN 10028-7 Grade X2CrNiMo17-12-3 Solution-Annealed Steel (+AT) – Superior Corrosion Resistance
    9. EN 10028‑7 X2CrNiMoN18‑12‑4 – Solution Annealed Austenitic Steel (+AT)
    10. EN 10028-7 Grade X2CrNiMo18-15-4 – Solution-Annealed Steel with Superior Corrosion Resistance