DIN 1652-3 Grade 16MnCr5 – Ferritic‑Pearlite Treatment & Cold‑Drawing for High‑Strength Automotive Components
The steel 16 MnCr 5 is used for larger parts with higher core strength and advantageous toughness properties in the vehicle and mechanical engineering (e.g. gears, shafts, steering parts). The lowest application amounts to -25 °C, the best application up to 50 mm nominal size.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.85 g/cm³ |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | -100.0 °C | 217 GPa |
20.0 °C | 212 GPa | |
100.0 °C | 207 GPa | |
200.0 °C | 199 GPa | |
300.0 °C | 192 GPa | |
400.0 °C | 184 GPa | |
500.0 °C | 175 GPa | |
600.0 °C | 164 GPa | |
Hardness, Brinell | 20.0 °C | 140 - 287 [-] |
Poisson's ratio | 20.0 °C | 0.28 [-] |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | -100.0 °C | 1.05E-5 1/K | |
20.0 °C | 1.15E-5 1/K | ||
100.0 °C | 1.21E-5 1/K | ||
200.0 °C | 1.27E-5 1/K | ||
300.0 °C | 1.32E-5 1/K | ||
400.0 °C | 1.36E-5 1/K | ||
500.0 °C | 1.4E-5 1/K | ||
600.0 °C | 1.44E-5 1/K | ||
Max service temperature, long | -25 - 0 °C | ||
Melting point | 1382 - 1529 °C | Typical for Chromium Steel | |
Specific heat capacity | -100.0 °C | 423 J/(kg·K) | |
20.0 °C | 461 J/(kg·K) | ||
100.0 °C | 479 J/(kg·K) | ||
200.0 °C | 499 J/(kg·K) | ||
300.0 °C | 517 J/(kg·K) | ||
400.0 °C | 536 J/(kg·K) | ||
500.0 °C | 558 J/(kg·K) | ||
600.0 °C | 587 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 45.9 W/(m·K) | |
100.0 °C | 46.4 W/(m·K) | ||
200.0 °C | 45.6 W/(m·K) | ||
300.0 °C | 43.5 W/(m·K) | ||
400.0 °C | 40.9 W/(m·K) | ||
500.0 °C | 38.2 W/(m·K) | ||
600.0 °C | 35.5 W/(m·K) | ||
Thermal diffusivity | 20.0 °C | 12.7 mm²/s | |
100.0 °C | 12 mm²/s | ||
200.0 °C | 11 mm²/s | ||
300.0 °C | 9.9 mm²/s | ||
400.0 °C | 8.7 mm²/s | ||
500.0 °C | 7.3 mm²/s | ||
600.0 °C | 6 mm²/s | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 2.27E-7 Ω·m |
100.0 °C | 2.76E-7 Ω·m | |
200.0 °C | 3.46E-7 Ω·m | |
300.0 °C | 4.31E-7 Ω·m | |
400.0 °C | 5.32E-7 Ω·m | |
500.0 °C | 6.48E-7 Ω·m | |
600.0 °C | 7.81E-7 Ω·m | |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.14 - 0.19 % |
Chromium | 0.8 - 1.1 % |
Manganese | 1 - 1.3 % |
Phosphorus | 0.04 % |
Silicon | 0.4 % |
Sulfur | 0.035 % |
Metal
- DIN 1652-3 Grade 20MoCrS4: Ferritic-Pearlite Structure & Cold-Drawn for High-Performance Applications
- DIN 1652-3 Grade 22CrMoS3-5: Ferritic‑Pearlite Heat Treatment & Cold‑Drawing for High‑Performance Automotive Components
- DIN 1652-3 Grade 20Cr4 Steel: Ferritic-Pearlitic Structure and Cold-Drawn Process for High-Wear Applications
- DIN 1652-3 Grade 20CrS4: Ferritic‑Pearlite Treatment & Cold‑Drawing for High‑Wear Applications
- DIN 1652-3 Grade 20MnCrS5: Ferritic-Pearlitic Structure and Cold-Drawn Processing
- DIN 1652‑3 Grade 20MoCr4 Steel – Ferritic‑Pearlite Structure & Cold‑Drawn for High‑Performance Applications
- DIN 1652-3 Grade 15CrNi6 – Ferritic‑Pearlite, Cold‑Drawn, High‑Toughness Steel for Vehicle Gears & Shafts
- DIN 1652-3 Grade 16MnCrS5: Ferritic‑Pearlitic Structure & Cold‑Drawn for Superior Strength
- DIN 1652-3: 17CrNiMo6 Steel – Ferritic–Pearlitic Treatment & Cold‑Drawn for High‑Load Applications
- DIN 1652-3 Grade 21NiCrMo2 – Ferritic-Pearlite Treated & Cold-Drawn Steel for High-Performance Mechanical Applications