EN 10263‑4 Grade 42CrMo4: Annealed for Spheroidized Carbides – High‑Performance Steel

The cold-upsettable steel 42 CrMo 4 can be cold-formed according to the usual forming methods on single-stage and multi-stage presses. Because of its high carbon content, only low to medium forming degrees are recommendable. It is used for screws of strength class 10.9 in the thick and of strength class 12.9 in the medium to thin dimension range.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Poisson's ratio

20.0 °C

0.28 [-]

Reduction of area

20.0 °C

58 %

Tensile strength

20.0 °C

630 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Melting point

1382 - 1529 °C

Typical for Chromium Molybdenum Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

45.1 W/(m·K)

100.0 °C

45.1 W/(m·K)

200.0 °C

44.1 W/(m·K)

300.0 °C

41.9 W/(m·K)

400.0 °C

39.4 W/(m·K)

500.0 °C

36.9 W/(m·K)

600.0 °C

34.4 W/(m·K)

Thermal diffusivity

20.0 °C

12.5 mm²/s

100.0 °C

11.6 mm²/s

200.0 °C

10.6 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.4 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.31E-7 Ω·m

100.0 °C

2.84E-7 Ω·m

200.0 °C

3.58E-7 Ω·m

300.0 °C

4.48E-7 Ω·m

400.0 °C

5.52E-7 Ω·m

500.0 °C

6.71E-7 Ω·m

600.0 °C

8.06E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.38 - 0.45 %

Chromium

0.9 - 1.2 %

Manganese

0.6 - 0.9 %

Molybdenum

0.15 - 0.3 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10263-4 Grade 41Cr4 Steel - Annealing for Spheroidized Carbides (+AC)
    2. EN 10263-4 Grade 46Cr2: Optimized Annealing for Spheroidized Carbides (+AC)
    3. EN 10263-4 Grade 30CrNiMo8 Steel – Annealed for Spheroidized Carbides (+AC)
    4. EN 10263-4 Grade 34Cr4: High-Performance Steel with Annealed Spheroidized Carbides (+AC)
    5. EN 10263-4 Grade 34CrNiMo6: Annealed for Spheroidized Carbides to Enhance Strength
    6. EN 10263‑4 Grade 37Cr4 Steel – Annealed for Spheroidized Carbides (+AC) – Superior Cold‑Forming & Strength Class 8.8
    7. EN 10263-4 Grade 38Cr2 Steel – Annealed for Spheroidized Carbides (+AC)
    8. EN 10269 42CrMo4 Steel – Annealed for Spheroidized Carbides (+AC)
    9. EN 10263-4 Grade 25CrMo4 Steel – Annealed for Spheroidized Carbides (AC)
    10. EN 10263-4 Grade 34CrMo4 – Annealed for Spheroidized Carbides (AC)