EN 10277-5 Grade 50CrV4: High-Performance Cold Drawn or Turned Steel for Heavy-Duty Applications

Steel 50 CrV 4 is suitable for high loaded parts that have to meet increased tempering and high wear resistance requirements at best core qualities in aircraft and vehicle construction and engine and machine engineering (e.g. transmission and joint parts, axles). Furthermore application to spring and tool steel. Lowest application temp. -25 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 - 212.6 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Hardness, Brinell

20.0 °C

248 [-]

Poisson's ratio

20.0 °C

0.29 [-]

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Max service temperature, long

-25 - 0 °C

Melting point

1382 - 1529 °C

Typical for Chromium Vanadium Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

45.1 W/(m·K)

100.0 °C

45.1 W/(m·K)

200.0 °C

44.1 W/(m·K)

300.0 °C

41.9 W/(m·K)

400.0 °C

39.4 W/(m·K)

500.0 °C

36.9 W/(m·K)

600.0 °C

34.4 W/(m·K)

Thermal diffusivity

20.0 °C

12.5 mm²/s

100.0 °C

11.6 mm²/s

200.0 °C

10.6 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.4 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.31E-7 Ω·m

100.0 °C

2.84E-7 Ω·m

200.0 °C

3.58E-7 Ω·m

300.0 °C

4.48E-7 Ω·m

400.0 °C

5.52E-7 Ω·m

500.0 °C

6.71E-7 Ω·m

600.0 °C

8.06E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.47 - 0.55 %

Chromium

0.9 - 1.2 %

Manganese

0.7 - 1.1 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.03 %

Vanadium

0.1 - 0.2 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. 25CrMo4 Steel – EN 10277-5 Cold Drawn, Soft Annealed, High Strength & Ductility
    2. EN 10277-5 Grade 25CrMoS4 – Cold‑Drawn, Turned & Soft‑Annealed High‑Strength Steel
    3. EN 10277-5 Grade 38CrS2: Cold Drawn/Turned & Soft Annealed Steel for High-Performance Applications
    4. EN 10277-5 Grade 41Cr4 – Cold-Drawn, Soft-Annealed Steel for Automotive & Mechanical Use
    5. EN 10277-5 Grade 41CrS4 Steel – Cold Drawn, Turned & Soft Annealed for Automotive & Industrial Applications
    6. EN 10277-5 Grade 42CrMo4: Cold Drawn, Turned & Soft Annealed Steel for High-Load Applications
    7. EN 10277-5 Grade 46Cr2 – Cold‑Drawn or Turned, Soft‑Annealed Steel for Automotive & Machine Applications
    8. EN 10277-5 Grade 46CrS2: Cold Drawn, Turned & Soft-Annealed Steel for High-Strength Automotive Parts
    9. EN 10277‑5 Grade 50CrMo4: Cold‑Drawn or Turned, Soft‑Annealed Steel for High‑Load Applications
    10. EN 10277-5 Grade 32Cr2 Steel – Cold Drawn, Turned, and Soft Annealed for High-Performance Vehicle and Engine Parts