EN 10277-5 Grade 50CrV4 Cold-Drawn Steel – High Strength & Wear Resistance

Steel 50 CrV 4 is suitable for high loaded parts that have to meet increased tempering and high wear resistance requirements at best core qualities in aircraft and vehicle construction and engine and machine engineering (e.g. transmission and joint parts, axles). Furthermore application to spring and tool steel. Lowest application temp. -25 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 - 212.6 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Poisson's ratio

20.0 °C

0.29 [-]

Tensile strength

20.0 °C

970 - 1050 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Max service temperature, long

-25 - 0 °C

Melting point

1382 - 1529 °C

Typical for Chromium Vanadium Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

45.1 W/(m·K)

100.0 °C

45.1 W/(m·K)

200.0 °C

44.1 W/(m·K)

300.0 °C

41.9 W/(m·K)

400.0 °C

39.4 W/(m·K)

500.0 °C

36.9 W/(m·K)

600.0 °C

34.4 W/(m·K)

Thermal diffusivity

20.0 °C

12.5 mm²/s

100.0 °C

11.6 mm²/s

200.0 °C

10.6 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.4 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.31E-7 Ω·m

100.0 °C

2.84E-7 Ω·m

200.0 °C

3.58E-7 Ω·m

300.0 °C

4.48E-7 Ω·m

400.0 °C

5.52E-7 Ω·m

500.0 °C

6.71E-7 Ω·m

600.0 °C

8.06E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.47 - 0.55 %

Chromium

0.9 - 1.2 %

Manganese

0.7 - 1.1 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.03 %

Vanadium

0.1 - 0.2 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10277-5 Grade 25CrMo4 Cold-Drawn Steel – High Strength & Ductility
    2. EN 10277-5 Grade 25CrMoS4 Cold-Drawn Steel – High Strength & Ductility for Automotive & Industrial Applications
    3. EN 10277-5 Grade 38Cr2 Cold Drawn Steel – High Strength & Low-Temperature Performance
    4. EN 10277-5 Grade 38CrS2 Cold Drawn Steel – Precision Alloy for Automotive and Machinery
    5. EN 10277‑5 Grade 41Cr4 Cold‑Drawn Steel – High‑Performance for Automotive & Machine Engineering
    6. EN 10277-5 Grade 41CrS4 Cold-Drawn Steel – High Strength for Automotive and Industrial Applications
    7. EN 10277-5 Grade 42CrMo4 – Premium Cold‑Drawn Steel for Heavy‑Duty Applications
    8. EN 10277‑5 Grade 46Cr2 Cold‑Drawn Steel – High Strength, Low Ductility for Vehicle Components
    9. EN 10277-5 Grade 46CrS2 Cold Drawn Steel – High Strength & Workability
    10. EN 10277-5 Grade 50CrMo4 Cold Drawn Steel – High‑Strength, Low‑Temperature Performance