JIS G4312 SUH660 Ageing After Solution Treatment: Performance & Properties
Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 7.9 - 8.2 g/cm³ | Typical for Austenitic Stainless Steel |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 195 GPa | Typical for Austenitic Stainless Steel |
Elongation A5 | 23.0 °C | 15 % | |
Hardness, Brinell | 23.0 °C | 248 [-] | |
Hardness, Rockwell C | 23.0 °C | 24 [-] | |
Hardness, Vickers | 23.0 °C | 261 [-] | |
Poisson's ratio | 23.0 °C | 0.3 [-] | Typical for Austenitic Stainless Steel |
Shear modulus | 23.0 °C | 77 GPa | Typical for Austenitic Stainless Steel |
Tensile strength | 23.0 °C | 900 MPa | |
Yield strength Rp0.2 | 23.0 °C | 590 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.7E-5 - 1.9E-5 1/K | Typical for Austenitic Stainless Steel |
Melting point | 1230 - 1480 °C | Typical for Austenitic Stainless Steel | |
Specific heat capacity | 23.0 °C | 440 J/(kg·K) | Typical for Austenitic Stainless Steel |
Thermal conductivity | 23.0 °C | 11 - 21 W/(m·K) | Typical for Austenitic Stainless Steel |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 8.5E-7 Ω·m | Typical for Austenitic Stainless Steel |
Technological properties
| Property | ||
|---|---|---|
| Processing history | ageing treatment after solution treatment | |
Metal
- Maximize Performance: JIS G4311 SUH38 Grade Ageing After Solution Treatment
- JIS G4311 SUH660 Stainless Steel: Post-Solution Ageing Treatment & Key Properties
- JIS G4311 Grade SUH37 – Optimized Ageing Treatment Following Solution Heat Treatment
- JIS G4311 Grade SUH661: Advanced Ageing Treatment Post Solution Processing
- Solution-Treated JIS G4312 Grade SUH660 Stainless Steel – Superior Mechanical Properties
- JIS G4312 SUH660 Ageing After Solution Treatment: Performance & Properties
- JIS G4312 SUH661: Optimized Ageing After Solution Treatment
- JIS G4312 Grade SUH661 – Solution Treated Stainless Steel: Key Properties & Specs
- JIS G4312 Grade SUH309 – Solution‑Treated Austenitic Stainless Steel Properties
- JIS G4312 Grade SUH310 Solution-Treated Stainless Steel: Comprehensive Property Overview