EN 1652 CuZn36 H120 – Premium Copper Alloy for High-Performance Applications

CuZn36 (CW507L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn33. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very good machinability: moderately hard soldering: good soft soldering: very good TIG-welding: moderately burnishing: very good CuZn36 is used for deep drawing components, pressure and punching components as well as for clockfaces. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.4 - 8.45 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

110 GPa

100.0 °C

106 GPa

200.0 °C

102 GPa

300.0 °C

97 GPa

400.0 °C

89 GPa

500.0 °C

79 GPa

Hardness, Vickers

20.0 °C

120 - 155 [-]

Poisson's ratio

20.0 °C

0.34 [-]

Shear modulus

23.0 °C

40 GPa

Typical for Wrought Copper Brass

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

150.0 °C

1.9E-5 1/K

300.0 °C

2.1E-5 1/K

650.0 °C

2.3E-5 1/K

800.0 °C

2.4E-5 1/K

Melting point

875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 J/(kg·K)

Thermal conductivity

-200.0 °C

50 W/(m·K)

20.0 °C

120 W/(m·K)

200.0 °C

142 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.50E+7 S/m

200.0 °C

1.20E+7 S/m

Electrical resistivity

20.0 °C

6.6E-8 Ω·m

200.0 °C

8.3E-8 Ω·m

Specific Electrical conductivity

26 % IACS

Chemical properties

PropertyValue

Aluminium

0.02 %

Copper

63.5 - 65.5 %

Iron

0.05 %

Lead

0.05 %

Nickel

0.3 %

Phosphorus

0.2 %

Tin

0.1 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 1652 CuZn36 H150 – Unhardenable Wrought Alloy for High-Strength Applications
    2. EN 1652 Grade CuZn36 H170: Premium Unhardenable Wrought Copper Alloy
    3. EN 1652 Grade CuZn20 H120 – Premium Copper‑Zinc Alloy for High‑Performance Applications
    4. EN 1652 Grade CuZn30 H120 – High-Strength Wrought Copper Alloy
    5. EN 1652 CuZn36 H055 – Unhardenable Copper Alloy with Superior Formability & Corrosion Resistance
    6. EN 1652 CuZn36 (H095) – High-Performance Wrought Copper Alloy
    7. EN 1652 Grade CuZn39Pb2 H120 – Unhardenable Brass Alloy with Enhanced Machinability
    8. EN 1652 Grade CuZn36 R480 – Unhardenable Wrought Alloy for High Strength Applications
    9. EN 1652 Grade CuZn36 R300 – Unhardenable Wrought Alloy with Superior Formability
    10. EN 1652 Grade CuZn36 R350: High-Strength, Unhardenable Copper Alloy for Precision Applications