EN 10277‑5 Grade 41CrS4: Soft‑Annealed, Cold‑Drawn Steel for Automotive & Machinery
Steel 41CrS4 is suitable for mean loaded parts in vehicle, engine and machine engineering with mean heat-treatment sections and enhanced workability. (e.g. gear wheels, transmission shafts, axles). Lowest application temperature -25°C. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.83 - 7.85 g/cm³ |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | -100.0 °C | 217 GPa |
20.0 °C | 210 - 212 GPa | |
100.0 °C | 205 - 207 GPa | |
200.0 °C | 195 - 199 GPa | |
300.0 °C | 185 - 192 GPa | |
400.0 °C | 175 - 184 GPa | |
500.0 °C | 175 GPa | |
600.0 °C | 164 GPa | |
Hardness, Brinell | 20.0 °C | 270 - 295 [-] |
Poisson's ratio | 20.0 °C | 0.28 [-] |
Shear modulus | 20.0 °C | 81 GPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | -100.0 °C | 1.05E-5 1/K | |
20.0 °C | 1.15E-5 1/K | ||
100.0 °C | 1.11E-5 - 1.21E-5 1/K | ||
200.0 °C | 1.21E-5 - 1.27E-5 1/K | ||
300.0 °C | 1.29E-5 - 1.32E-5 1/K | ||
400.0 °C | 1.35E-5 - 1.36E-5 1/K | ||
500.0 °C | 1.4E-5 1/K | ||
600.0 °C | 1.44E-5 1/K | ||
Max service temperature, long | -25 - 0 °C | ||
Melting point | 1382 - 1529 °C | Typical for Chromium Steel | |
Specific heat capacity | -100.0 °C | 423 J/(kg·K) | |
20.0 °C | 460 - 461 J/(kg·K) | ||
100.0 °C | 479 J/(kg·K) | ||
200.0 °C | 499 J/(kg·K) | ||
300.0 °C | 517 J/(kg·K) | ||
400.0 °C | 536 J/(kg·K) | ||
500.0 °C | 558 J/(kg·K) | ||
600.0 °C | 587 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 45.1 - 46 W/(m·K) | |
100.0 °C | 45.1 W/(m·K) | ||
200.0 °C | 44.1 W/(m·K) | ||
300.0 °C | 41.9 W/(m·K) | ||
400.0 °C | 39.4 W/(m·K) | ||
500.0 °C | 36.9 W/(m·K) | ||
600.0 °C | 34.4 W/(m·K) | ||
Thermal diffusivity | 20.0 °C | 12.5 mm²/s | |
100.0 °C | 11.6 mm²/s | ||
200.0 °C | 10.6 mm²/s | ||
300.0 °C | 9.5 mm²/s | ||
400.0 °C | 8.4 mm²/s | ||
500.0 °C | 7.1 mm²/s | ||
600.0 °C | 5.8 mm²/s | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 1.9E-7 - 2.31E-7 Ω·m |
100.0 °C | 2.84E-7 Ω·m | |
200.0 °C | 3.58E-7 Ω·m | |
300.0 °C | 4.48E-7 Ω·m | |
400.0 °C | 5.52E-7 Ω·m | |
500.0 °C | 6.71E-7 Ω·m | |
600.0 °C | 8.06E-7 Ω·m | |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.38 - 0.45 % |
Chromium | 0.9 - 1.2 % |
Manganese | 0.6 - 0.9 % |
Phosphorus | 0.03 - 0.04 % |
Silicon | 0.4 % |
Sulfur | 0.02 - 0.04 % |
Metal
- EN 10277-5 Grade 42CrMoS4 Soft Annealed & Cold Drawn (A+C) – High-Performance Steel for Automotive & Machine Applications
- EN 10277-4: Grade 20MnCrS5 Soft‑Annealed and Cold‑Drawn Steel (+A+C)
- 25CrMo4 Steel – EN 10277-5 Cold Drawn, Soft Annealed, High Strength & Ductility
- EN 10277-5 Grade 25CrMoS4 – Cold‑Drawn, Turned & Soft‑Annealed High‑Strength Steel
- EN 10277-5 Grade 38CrS2: Cold Drawn/Turned & Soft Annealed Steel for High-Performance Applications
- EN 10277-5 Grade 41CrS4 Steel – Cold Drawn, Turned & Soft Annealed for Automotive & Industrial Applications
- EN 10277-5 Grade 51CrV4 Steel – Soft Annealed, Cold Drawn for High-Performance Applications
- EN 10277-5 Grade 25CrMoS4 Soft Annealed & Cold Drawn Steel (+A+C) – Premium High‑Strength, Ductility for Automotive & Machine Use
- EN 10277-5 Grade 34CrNiMo6: Soft Annealed & Cold Drawn Steel for High-Performance Applications
- EN 10277-5 Grade 34CrS4: Soft-Annealed & Cold-Drawn Steel for Automotive & Industrial Applications