ASTM B316 Grade 2117 O Aluminium Alloy – Key Properties & Applications
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.75 - 2.84 g/cm³ | Typical for Wrought 2000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 70.0 - 73.0 GPa | Typical for Wrought 2000 Series Aluminium | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Shear modulus | 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | |||
Tensile strength | 175.0 | O | ASTM B316 | Wire, Rod |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Melting point | 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Specific heat capacity | 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Thermal conductivity | 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 | O | ASTM B316 | Wire, Rod |
Copper | 2.2 - 3.0 % | O | ASTM B316 | Wire, Rod |
Iron | 0.7 | O | ASTM B316 | Wire, Rod |
Magnesium | 0.2 - 0.5 % | O | ASTM B316 | Wire, Rod |
Manganese | 0.2 | O | ASTM B316 | Wire, Rod |
Silicon | 0.8 | O | ASTM B316 | Wire, Rod |
Zinc | 0.25 | O | ASTM B316 | Wire, Rod |
Technological properties
| Property | ||
|---|---|---|
| Workability | Moderate Workability | |
Metal
- ASTM B316 Grade 2117 H15 Aluminum Alloy – Key Properties & Applications
- ASTM B316: Grade 2117 H13 – Key Properties & Standards
- ASTM B316 Grade 5056 H32 Aluminium Alloy – Properties & Specifications
- ASTM B316 Grade 5056-O: Premium 5000-Series Aluminum Alloy
- ASTM B316 Grade 2117 T4 – High-Strength 2000 Series Aluminum Alloy
- ASTM B316 Grade 6061-O Aluminum: High-Performance Alloy for Corrosion Resistance and Fabrication
- ASTM B316 Grade 7050-O: High-Performance Heat‑Treatable Aluminum Alloy for Aerospace
- ASTM B316 Grade 7075 Aluminum Alloy – Superior Strength & Corrosion Resistance for Aerospace Applications
- ASTM B316 Grade 2024-O: High‑Strength Aerospace Aluminum Alloy
- ASTM B316 Grade 1100 O Aluminum Alloy – Superior Corrosion Resistance & Purest 1000 Series