99.98% Pure Nickel Rod & Wire – Full Hard, High Conductivity & Superior Oxidation Resistance

Nickel with highest degree of purity with the following features:

Very low levels of carbon (20 ppm) and sulfur (2 ppm) which tend to segregate at grain boundries resulting in hot shortening

Cleanliness, absence of non-metallic inclusions as Al, Ti or Si oxides

Low electrical resistivity at 20°C

High thermal conductivity at 20°C

Excellent formability

Low softening temperature (350°C)

Low recrystallization temperature (350°C)

Improved oxidation resistance: development of tightly adherent one-layer oxide scale instead of a two-layer costumary one, which tends to flake off due to mismatch in thermal expansion.

Properties

Dimension

Property	Value
Dimensions	Rod: Diameter: up to 4.7 mm, Length: up to 2500 mm - Wire: Diameter: 0.2-1.6 mm ; various dimensions can be also customized

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	196 GPa
Hardness, Vickers	23.0 °C	150 [-]	min.

Thermal

Property	Temperature	Value
Recrystallization temperature		350 °C
Thermal conductivity	23.0 °C	90.9 - 91 W/(m·K)

Electrical

Property	Temperature	Value
Electrical resistivity	23.0 °C	7.1E-8 Ω·m

Chemical properties

Property	Value
Carbon	2E-3 %
Nickel	99.98 %
Sulfur	2E-4 %

Technological properties

Property
Application areas	Wire: Sputter Targets, evaporation pellets, regulator coil in glow plugs of diesel engines; litz wire for current conduction under elevated temperatures and in aggressive environments, Pre material for thin wire manfacturing, Ni wire mesh, Thermal Spraying, Coating layer for corrosion protection from alkalis; salt spray; molten salt and reduciing chemicals; coating layer for high temperature resistance; corrosion protection at high temperatures; coating layer for membrane walls of power plants
Heat Treatment	Full Hardened
Processing history	For producing wire, the 6 mm hot rolled thick plates are cut into 6 mm wide sticks. The sticks are frontally welded. Afterwards the raw wire can be treated in the same way as hot rolled wire produced by melt metallurgy. accordingly, the wire is drawn to the desired dimensions through cold drawing and intermediate annealing.
Surface Finish	Blank/Bare/bright surface

99.98% Pure Nickel Rod & Wire – 1/2 Hard, Ultra-Low Carbon & Sulfur, High Conductivity, Superior Formability 99.98% Pure Nickel Flat Wire – S-Annealed for Superior Performance