EN 12168 Grade CuZn40 H100 – High-Strength, Unhardenable Wrought Alloy

CuZn40 (CW509L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn37. Corrosion resistance is similar to pure copper. Processing properties: warm forming: very good cold forming: good machinability: moderately hard soldering: good soft soldering: very good TIG-welding: moderately burnishing: very good CuZn40 is used for hot-pressed forgings, metal fitting and lock components, for nipple wire, condenser bottoms and watchcases.

Properties

General

Property	Temperature	Value
Density	20.0 °C	8.4 - 8.41 g/cm³

Mechanical

Property	Temperature	Value
Elastic modulus	20.0 °C	102 GPa
	100.0 °C	99 GPa
	200.0 °C	94 GPa
	300.0 °C	89 GPa
	400.0 °C	83 GPa
	500.0 °C	74 GPa
	600.0 °C	64 GPa
	700.0 °C	54 GPa

Hardness, Brinell	20.0 °C	95 - 145 [-]
Hardness, Vickers	20.0 °C	100 - 160 [-]
Poisson's ratio	20.0 °C	0.34 [-]
Shear modulus	20.0 °C	37 GPa

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	1.7E-5 - 2.1E-5 1/K	Typical for Wrought Copper Brass
Melting point		875 - 1075 °C	Typical for Wrought Copper Brass
Specific heat capacity	20.0 °C	375 - 377 J/(kg·K)
Thermal conductivity	20.0 °C	109 - 117 W/(m·K)

Electrical

Property	Temperature	Value
Electrical conductivity	20.0 °C	1.39E+7 - 1.50E+7 S/m
Electrical resistivity	20.0 °C	6.7E-8 Ω·m
Specific Electrical conductivity		24 - 26 % IACS

Chemical properties

Property	Value
Aluminium	0.05 %
Copper	59 - 61.5 %
Iron	0.2 %
Lead	0.2 - 0.3 %
Nickel	0.3 %
Tin	0.2 %