EN 10088‑1 Grade X2CrMoTiS18‑2 Soft‑Annealed Steel (+A) – Premium Ferritic Properties
The ferritic material X2CrMoTiS18-2 as a patented steel is used in the form of rods, wire rod and profiles. No resistance to intercrystalline corrosion in welded condition.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.7 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 220 GPa | |
100.0 °C | 215 GPa | ||
200.0 °C | 210 GPa | ||
300.0 °C | 205 GPa | ||
400.0 °C | 195 GPa | ||
Elongation | 20.0 °C | 15 % | |
Hardness, Brinell | 20.0 °C | 200 [-] | |
Poisson's ratio | 23.0 °C | 0.3 [-] | Typical for Ferritic Stainless Steel |
Shear modulus | 23.0 °C | 77 GPa | Typical for Ferritic Stainless Steel |
Tensile strength | 20.0 °C | 430 - 600 MPa | |
Yield strength Rp0.2 | 20.0 °C | 280 MPa | |
100.0 °C | 250 MPa | ||
150.0 °C | 240 MPa | ||
200.0 °C | 230 MPa | ||
250.0 °C | 220 MPa | ||
300.0 °C | 210 MPa | ||
350.0 °C | 205 MPa | ||
400.0 °C | 200 MPa | ||
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.04E-5 1/K | |
200.0 °C | 1.08E-5 1/K | ||
300.0 °C | 1.12E-5 1/K | ||
400.0 °C | 1.16E-5 1/K | ||
500.0 °C | 1.19E-5 1/K | ||
Melting point | 1425 - 1530 °C | Typical for Ferritic Stainless Steel | |
Specific heat capacity | 20.0 °C | 430 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 23 W/(m·K) | |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 8E-7 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.03 % |
Chromium | 17.5 - 19 % |
Manganese | 0.5 % |
Molybdenum | 2 - 2.5 % |
Phosphorus | 0.04 % |
Silicon | 1 % |
Sulfur | 0.15 - 0.35 % |
Titanium | 0.3 - 0.8 % |
Metal
- EN 10088-1 X70CrMo15: Soft Annealed Grade for Cutting Tools & Industrial Applications
- X105CrMo17 Soft Annealed Steel (EN 10088-1) – High Hardening & Wear Resistance
- EN 10088-1 Grade X90CrMoV18 – Soft Annealed Steel for High‑Performance Cutting Tools
- EN 10088-1 X50CrMoV15 Soft-Annealed Steel: High Strength & Abrasion Resistance
- EN 10088-1 Grade X2CrMoTi29-4 Soft-Annealed Steel for Cold-Rolled Strips
- EN 10088-1 Grade X2CrAlTi18-2 Soft-Annealed Steel – Superior Corrosion Resistance & Mechanical Performance
- EN 10088-1 X6CrNi17-1 Soft‑Annealed Steel (+A) – High Corrosion Resistance & Strength
- EN 10088‑1 X6CrNiTi12 Soft‑Annealed Steel – Grade X6CrNiTi12 (+A) – Specifications & Properties
- EN 10088-1 X2CrMoTi17-1 Soft Annealed Steel – Superior Formability for Appliances & Pipes
- EN 10088-1 Grade X2CrNbZr17 Soft Annealed Steel (+A) – Superior Corrosion & Heat Resistance