EN 10088‑1 X6CrNiTi12 Soft‑Annealed Steel – Grade X6CrNiTi12 (+A) – Specifications & Properties
Material X6CrNiTi12 is a ferritic steel which is used in annealed condition for cold rolled strip as well as for warm rolled strip and sheet. It does not show resistance to intercrystalline corrosion both in delivery and welded condition.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.7 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 220 GPa | |
100.0 °C | 215 GPa | ||
200.0 °C | 210 GPa | ||
300.0 °C | 205 GPa | ||
400.0 °C | 195 GPa | ||
Elongation | 20.0 °C | 20 - 23 % | |
Elongation A80 | 20.0 °C | 20 - 23 % | |
Elongation A80, transverse | 20.0 °C | 20 - 23 % | |
Elongation, transverse | 20.0 °C | 20 - 23 % | |
Poisson's ratio | 23.0 °C | 0.3 [-] | Typical for Ferritic Stainless Steel |
Shear modulus | 23.0 °C | 77 GPa | Typical for Ferritic Stainless Steel |
Tensile strength | 20.0 °C | 450 - 650 MPa | |
Tensile strength, transverse | 20.0 °C | 450 - 650 MPa | |
Yield strength Rp0.2 | 20.0 °C | 250 - 280 MPa | |
100.0 °C | 300 MPa | ||
150.0 °C | 270 MPa | ||
200.0 °C | 250 MPa | ||
250.0 °C | 245 MPa | ||
300.0 °C | 225 MPa | ||
350.0 °C | 215 MPa | ||
Yield strength Rp0.2, transverse | 20.0 °C | 280 - 320 MPa | |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.05E-5 1/K | |
300.0 °C | 1.15E-5 1/K | ||
Melting point | 1425 - 1530 °C | Typical for Ferritic Stainless Steel | |
Specific heat capacity | 20.0 °C | 460 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 30 W/(m·K) | |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 6E-7 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.08 % |
Chromium | 10.5 - 12.5 % |
Manganese | 1.5 % |
Nickel | 0.5 - 1.5 % |
Phosphorus | 0.04 % |
Silicon | 0.7 % |
Sulfur | 0.015 % |
Titanium | 0.05 - 0.35 % |
Metal
- EN 10088-1 X70CrMo15: Soft Annealed Grade for Cutting Tools & Industrial Applications
- X105CrMo17 Soft Annealed Steel (EN 10088-1) – High Hardening & Wear Resistance
- EN 10088-1 Grade X90CrMoV18 – Soft Annealed Steel for High‑Performance Cutting Tools
- EN 10088‑1 Grade X2CrMoTiS18‑2 Soft‑Annealed Steel (+A) – Premium Ferritic Properties
- EN 10088-1 X50CrMoV15 Soft-Annealed Steel: High Strength & Abrasion Resistance
- EN 10088-1 Grade X2CrMoTi29-4 Soft-Annealed Steel for Cold-Rolled Strips
- EN 10088-1 Grade X2CrAlTi18-2 Soft-Annealed Steel – Superior Corrosion Resistance & Mechanical Performance
- EN 10088-1 X6CrNi17-1 Soft‑Annealed Steel (+A) – High Corrosion Resistance & Strength
- EN 10088-1 X2CrMoTi17-1 Soft Annealed Steel – Superior Formability for Appliances & Pipes
- EN 10088-1 Grade X2CrNbZr17 Soft Annealed Steel (+A) – Superior Corrosion & Heat Resistance