EN 10095 X10NiCrSi35-19: Solution-Annealed Steel for High-Temperature Applications up to 1100°C

Steel X10NiCrSi35-19 shows a highest application temperature of up to 1100 °C in air.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

190 - 210 GPa

Typical for Steel

Elongation

20.0 °C

40 %

Hardness, Brinell

20.0 °C

200 [-]

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Steel

Tensile strength

20.0 °C

500 - 650 MPa

Yield strength Rp0.2

20.0 °C

270 MPa

Yield strength Rp1.0

20.0 °C

300 MPa

Thermal

PropertyTemperatureValue

Coefficient of thermal expansion

200.0 °C

1.55E-5 1/K

400.0 °C

1.6E-5 1/K

600.0 °C

1.7E-5 1/K

800.0 °C

1.77E-5 1/K

1000.0 °C

1.8E-5 1/K

Max service temperature, long

0 - 1100 °C

Specific heat capacity

20.0 °C

460 J/(kg·K)

600.0 °C

650 J/(kg·K)

Thermal conductivity

20.0 °C

12 W/(m·K)

500.0 °C

19.5 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.15 %

Chromium

17 - 20 %

Manganese

2 %

Nickel

33 - 37 %

Nitrogen

0.11 %

Phosphorus

0.03 %

Silicon

1 - 2 %

Sulfur

0.015 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10095 NiCr20Ti Alloy – Solution Annealed (With AT)
    2. EN 10095 NiCr23Fe Alloy – Solution Annealed for Superior High‑Temperature Oxidation Resistance
    3. EN 10095 X6NiCrSiNCe35-25 – Solution Annealed, High‑Temperature Stainless Steel
    4. EN 10095 X12NiCrSi35-16 Solution-Annealed Alloy – High‑Temperature Stability & Low Embrittlement
    5. EN 10095 X25CrMnNiN25-9-7 Stainless Steel – Solution Annealed with Additional Treatment
    6. EN 10095 X10NiCrSiNb35-22 Duplex Stainless Steel – Solution Annealed & Aged for High‑Temperature Performance
    7. EN 10095 Grade X6CrNiSiNCe19-10 – Solution Annealed Stainless Steel for High-Temperature Applications
    8. EN 10095 X9CrNiSiNCe21-11-2: High-Temperature Solution-Annealed Austenitic Steel (+AT)
    9. EN 10095 Grade X8CrNiTi18-10 – Solution Annealed Steel for High-Load Applications
    10. EN 10095 Grade X10NiCrAlTi32‑21 – Solution Annealed Steel for High‑Temperature Pressure Applications