EN 10277-3 Grade 46S20 Steel – Rolled & Turned (+SH) for High‑Strength Cutting Applications

The free cutting case hardening steel 46S20 is used for bulk parts of high strength, especially for low ductility demands in transversal direction compared to other C-steels (e.g. C45). Cutting speed is increased but higher cracking risk according to rising C-content has to be considered. Application in car industry, apparatus, equipment and machine engineering (e.g. screws, nuts, small-size parts). As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 - 7.85 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

207 GPa

200.0 °C

193 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Hardness, Brinell

20.0 °C

166 - 225 [-]

Poisson's ratio

25.0 °C

0.28 [-]

Shear modulus

20.0 °C

81 GPa

Tensile strength

20.0 °C

560 - 760 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.1E-5 - 1.25E-5 1/K

200.0 °C

1.18E-5 - 1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.32E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1380 - 1514 °C

Typical for Medium Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 - 490 J/(kg·K)

200.0 °C

499 - 530 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 - 600 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

41.7 - 49 W/(m·K)

100.0 °C

43.4 W/(m·K)

200.0 °C

43.2 W/(m·K)

300.0 °C

41.4 W/(m·K)

400.0 °C

39.1 W/(m·K)

500.0 °C

36.7 W/(m·K)

600.0 °C

34.1 W/(m·K)

Thermal diffusivity

20.0 °C

11.6 mm²/s

100.0 °C

11.3 mm²/s

200.0 °C

10.5 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.3 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.2E-7 - 2.5E-7 Ω·m

100.0 °C

2.95E-7 Ω·m

200.0 °C

3.65E-7 Ω·m

300.0 °C

4.53E-7 Ω·m

400.0 °C

5.56E-7 Ω·m

500.0 °C

6.74E-7 Ω·m

600.0 °C

8.13E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.42 - 0.5 %

Manganese

0.7 - 1.1 %

Phosphorus

0.06 %

Silicon

0.4 %

Sulfur

0.15 - 0.25 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10277-3 Grade 35SPb20 – Rolled & Turned Steel with Hardening + SH
    2. Grade 38SMn28 Steel (EN 10277-3): Rolled & Turned – High-Strength, Shaded Hardening Option
    3. EN 10277‑3 Grade 46SPb20 Rolled & Turned Steel (+SH) – High Strength, Low Ductility
    4. EN 10277-3 Grade 35S20: Rolled & Turned Steel with Surface Hardening
    5. EN 10277-3: Grade 11SMnPb30 – Rolled & Turned Steel for Automotive & Equipment Applications
    6. EN 10277-3 Grade 11SMnPb37 – Rolled & Turned Steel (Superheated)
    7. EN 10277-3 Grade 10SPb20: Rolled & Turned Case-Hardened Steel (+SH)
    8. EN 10277‑3 Grade 10S20 – Rolled, Turned & Surface‑Hardened (SH) Steel
    9. EN 10277-3: 11SMn30 Grade Steel – Rolled, Turned, and Surface-Hardened
    10. EN 10277-3 11SMn37 Steel: Rolled & Turned Grade with Superior Surface Finish