JIS H4100 Grade 1100 – High‑Purity 99% Aluminum Alloy
JIS 1100 is a soft, non-heat-treatable and low strength alloy that offers strong corrosion resistance. Composed of 99% aluminum and 0.12% copper, JIS 1100 is purest grade of aluminum alloy available commercially.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.7 g/cm³ | Typical for Wrought 1000 Series Aluminium |
Mechanical
| Property | Value | Related Standards | Comment |
|---|---|---|---|
Elastic modulus | 68.0 - 70.0 GPa | Typical for Wrought 1000 Series Aluminium | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | |
Poisson's ratio | 0.33 [-] | Typical for Wrought 1000 Series Aluminium | |
Shear modulus | 25.9 GPa | Typical for Wrought 1000 Series Aluminium | |
Tensile strength | 78.0 MPa | JIS H4100 | |
Yield strength | 20.0 MPa | JIS H4100 |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.5e-05 1/K | Typical for Wrought 1000 Series Aluminium |
Melting point | 645.0 - 660.0 °C | Typical for Wrought 1000 Series Aluminium |
Specific heat capacity | 900.0 - 963.0 J/(kg·K) | Typical for Wrought 1000 Series Aluminium |
Thermal conductivity | 167.0 - 244.0 W/(m·K) | Typical for Wrought 1000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 33000000.0 - 38000000.0 S/m | Typical for Wrought 1000 Series Aluminium |
Electrical resistivity | 2.7e-08 - 3e-08 Ω·m | Typical for Wrought 1000 Series Aluminium |
Technological properties
| Property | ||
|---|---|---|
| Brazing | Excellent | |
| Workability | Excellent workability. | |
Metal
- JIS H4100 Grade 1200 Aluminium – Comprehensive Properties & Standards
- JIS H4100 Grade 7N01 O Aluminium: Key Properties & Standards
- JIS H4100 Grade 7N01 T4 Aluminium – Key Properties & Standards
- JIS H4100 5083 Aluminum Alloy – Key Mechanical Properties
- JIS H4100 Grade 5083 O Aluminium – Key Properties & Standards
- JIS Z3232 Grade 1100 O Aluminum: Superior Corrosion Resistance & High Purity
- JIS H4100 Grade 6063 Aluminum Alloy – High Corrosion Resistance & Superior Finish
- JIS H4040 Grade 1100 – Pure Aluminum Alloy with Superior Corrosion Resistance
- JIS H4100 2024-O Aluminum Alloy – High Strength, Aircraft‑Grade Performance
- JIS 6063 T6 Aluminum – Durable, Corrosion-Resistant Architectural Alloy