JIS H4100 Grade 6063 Aluminum Alloy – High Corrosion Resistance & Superior Finish
Aluminum JIS 6063 is an architectural alloy that offers users a high resistance to corrosion and excellent finishing characteristics. Easy to extrude with fair machinability, JIS 6063 can be both hot and cold formed and is commonly available as T6 temper as well as T4 temper.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.7 g/cm³ | Typical for Wrought 6000 Series Aluminium |
Mechanical
| Property | Value | Related Standards | Comment |
|---|---|---|---|
Elastic modulus | 70.0 GPa | Typical for Wrought 6000 Series Aluminium | |
Elongation | 12.0 % | JIS H4100 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | |
Poisson's ratio | 0.33 [-] | Typical for Wrought 6000 Series Aluminium | |
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | |
Tensile strength | 118.0 MPa | JIS H4100 | |
Yield strength | 49.0 MPa | JIS H4100 |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 6000 Series Aluminium |
Melting point | 555.0 - 655.0 °C | Typical for Wrought 6000 Series Aluminium |
Specific heat capacity | 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium |
Thermal conductivity | 170.0 - 220.0 W/(m·K) | Typical for Wrought 6000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 21000000.0 - 34000000.0 S/m | Typical for Wrought 6000 Series Aluminium |
Electrical resistivity | 2.9e-08 - 5e-08 Ω·m | Typical for Wrought 6000 Series Aluminium |
Technological properties
| Property | ||
|---|---|---|
| Workability | Excellent workability. | |
Metal
- JIS H4100 Grade 1200 Aluminium – Comprehensive Properties & Standards
- JIS H4100 Grade 7N01 O Aluminium: Key Properties & Standards
- JIS H4100 5083 Aluminum Alloy – Key Mechanical Properties
- JIS H4040 Grade 6063: High-Performance Aluminum Alloy for Architecture
- JIS 6063 Aluminum Alloy – Durable, Corrosion‑Resistant Architectural Grade
- JIS H4100 Grade 1100 – High‑Purity 99% Aluminum Alloy
- JIS H4100 Grade 6063: Quick-Cooled, Artificially Aged Aluminum Alloy
- JIS 6063 T6 Aluminum – Durable, Corrosion-Resistant Architectural Alloy
- JIS H4040 Grade 6063 T6 Aluminum Alloy – Corrosion-Resistant & Superior Finish
- JIS H4080 Grade 6063 T6 Aluminum Alloy – High Corrosion Resistance & Superior Finish