EN 12164 Grade CuZn38Pb1 R360 – Premium Cold‑Formable Brass Alloy
CW607N is good to very good cold formable and machinable. Application: bending, riveting, embossing and upsetting parts
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.4 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 102 GPa | |
Elongation | 20.0 °C | 20 - 25 % | |
Elongation A100 | 20.0 °C | 10 % | |
Elongation A11.3 | 20.0 °C | 15 % | |
Shear modulus | 23.0 °C | 40 GPa | Typical for Wrought Copper Brass |
Tensile strength | 20.0 °C | 360 MPa | |
Yield strength Rp0.2 | 20.0 °C | 150 - 300 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.7E-5 - 2.1E-5 1/K | Typical for Wrought Copper Brass |
Melting point | 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 20.0 °C | 377 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 109 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 1.39E+7 S/m |
Specific Electrical conductivity | 24 % IACS |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 0.05 % |
Copper | 60 - 61 % |
Iron | 0.2 % |
Lead | 0.8 - 1.6 % |
Nickel | 0.3 % |
Tin | 0.2 % |
Metal
- EN 12166 Grade CuZn36 R360 – Premium Beryllium Copper Alloy
- EN 12164 CuZn38Pb1 (R490) Brass – Key Mechanical & Thermal Properties
- EN 12164 Grade CuZn38Pb2 R490 – Premium Wrought Copper Brass Specification
- EN 12164 Grade CuPb1P R360 – High Conductivity, Low Alloy Copper for Precision Applications
- EN 12164 Grade CuSP R360 – Unhardenable Low‑Alloy Copper for Precision Applications
- EN 12164 CuZn39Pb0.5 R360 Brass – Superior Strength & Machinability
- EN 12164 Grade CuTeP R360 – Superior Copper Alloy for Machining & Corrosion Resistance
- EN 12164 R360 CuZn39Pb3 Brass – Unhardenable Alloy with High Strength and Improved Machinability
- EN 12164 CuZn40Pb2 R360 – High Strength, Low Hardness, Superior Machinability
- EN 12164 CuZn38Pb1 Grade – 410 MPa Copper–Zinc–Lead Alloy